EN 12164 Grade CuTeP R360 – Superior Copper Alloy for Machining & Corrosion Resistance
CuTeP, mat. No CW118C, is counted among unhardenable, low alloyed copper alloys. To the comparable make CuTeP, mat. No 2.1546, acc. to DIN 17666 : 1983-12 applies: A strength increase is achievable only by cold forming. CuTeP is applicated as free-cutting alloy due to its favorable machinability. The alloy shows a higher temperature for removal of workhardening (350°C) compared to pure copper. CuTeP shows roughly the same electrical conductivity and corrosion resistance as copper. Processing properties: hot forming: very good cold forming: good machinability: very good soft and hard soldering: good gas shielded welding: good burnishing: good Application: In electronics and electrical engineering, e.g. for small parts such as diode bases and transistors. For welding torch nozzles, screws, nuts, parts for screw connections and fitting components.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.8 - 8.9 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 120 GPa | |
Elongation | 20.0 °C | 5 % | |
Hardness, Brinell | 20.0 °C | 120 [-] | |
Poisson's ratio | 23.0 °C | 0.34 [-] | Typical for Wrought Copper Pure / Low Alloyed Copper |
Shear modulus | 23.0 °C | 48 GPa | Typical for Wrought Copper Pure / Low Alloyed Copper |
Tensile strength | 20.0 °C | 360 MPa | |
Yield strength Rp0.2 | 20.0 °C | 300 - 320 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 300.0 °C | 1.8E-5 1/K | |
Melting point | 965 - 1100 °C | Typical for Wrought Copper Pure / Low Alloyed Copper | |
Specific heat capacity | 23.0 °C | 377 - 420 J/(kg·K) | Typical for Wrought Copper Pure / Low Alloyed Copper |
Thermal conductivity | 20.0 °C | 368 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 5.00E+7 - 5.45E+7 S/m |
Specific Electrical conductivity | 86 % IACS |
Chemical properties
| Property | Value |
|---|---|
Phosphorus | 0 - 0.01 % |
Tellurium | 0.4 - 0.7 % |
Metal
- EN 12166 Grade CuZn36 R360 – Premium Beryllium Copper Alloy
- EN 12164 Grade CuPb1P R360 – High Conductivity, Low Alloy Copper for Precision Applications
- EN 12164 Grade CuSP R360 – Unhardenable Low‑Alloy Copper for Precision Applications
- EN 12168 Grade CuTeP H080: High-Performance Copper Alloy for Superior Machining
- EN 12164 Grade CuZn38Pb1 R360 – Premium Cold‑Formable Brass Alloy
- EN 12164 CuZn39Pb0.5 R360 Brass – Superior Strength & Machinability
- EN 12164 R360 CuZn39Pb3 Brass – Unhardenable Alloy with High Strength and Improved Machinability
- EN 12164 CuZn40Pb2 R360 – High Strength, Low Hardness, Superior Machinability
- EN 12164 Grade CuTeP R250 – Premium Low‑Alloy Copper Alloy for Precision Machining
- EN 12164 Grade CuTeP R300 – Premium Low‑Alloy Copper Alloy for Superior Machinability