EN 12163 Grade CuZn36 R310 – Premium Unhardenable Copper Alloy for High-Performance Applications

CuZn36 (CW507L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn33. Corrosion resistance is similar to pure copper. Processing properties: warm forming: good cold forming: very good machinability: moderately hard soldering: good soft soldering: very good TIG-welding: moderately burnishing: very good CuZn36 is used for deep drawing components, pressure and punching components as well as for clockfaces. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.4 - 8.45 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

110 GPa

100.0 °C

106 GPa

200.0 °C

102 GPa

300.0 °C

97 GPa

400.0 °C

89 GPa

500.0 °C

79 GPa

Elongation

20.0 °C

30 %

Elongation A10

20.0 °C

25 %

Elongation A100

20.0 °C

20 %

Shear modulus

23.0 °C

40 GPa

Typical for Wrought Copper Brass

Tensile strength

20.0 °C

310 MPa

Yield strength Rp0.2

20.0 °C

120 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

150.0 °C

1.9E-5 1/K

300.0 °C

2.1E-5 1/K

650.0 °C

2.3E-5 1/K

800.0 °C

2.4E-5 1/K

Melting point

875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

377 J/(kg·K)

Thermal conductivity

-200.0 °C

50 W/(m·K)

20.0 °C

120 W/(m·K)

200.0 °C

142 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

1.50E+7 S/m

200.0 °C

1.20E+7 S/m

Electrical resistivity

20.0 °C

6.6E-8 Ω·m

200.0 °C

8.3E-8 Ω·m

Chemical properties

PropertyValue

Aluminium

0.02 %

Copper

63.5 - 65 %

Iron

0.05 %

Lead

0.05 %

Nickel

0.3 %

Tin

0.1 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 12163 CuZr TH Grade – High Strength Low‑Alloy Copper Alloy
    2. EN 12163 Grade CuZn36 M – Premium Unhardenable Copper Alloy for Precision Deep Drawing
    3. EN 12163 CuZn36 R440 – Premium Unhardenable Wrought Copper Alloy
    4. EN 12163 CuZn36 H070 – High-Strength, Corrosion-Resistant Copper Alloy
    5. EN 12163 Grade CuZn36 H105 – Premium Copper Alloy for High-Performance Applications
    6. EN 12163 Grade CuZn36 – High-Performance Unhardenable Copper Alloy
    7. EN 12163 Grade CuZn37 R310 – High-Strength Unhardenable Copper Alloy for Cold Forming
    8. EN 12163 Grade CuZn28 (R310) – Premium High‑Strength Copper Alloy
    9. EN 12163 CuZn33 R310 – Premium Grade Alloy for High-Performance Applications
    10. EN 12163 CuZn36 (R370) – High‑Strength, Low‑Conductivity Copper Alloy