EN 10277-5 Grade 34CrNiMo6 – Cold-Drawn, Turned, Quenched & Tempered Steel for High-Load Applications

Steel 34 CrNiMo 6 is suitable for high loaded parts (also heavy forged parts) of high heat-treatment sections and favorable ductility qualities in aircraft and heavy-vehicle construction and in machine engineering (e.g. propeller shafts, connecting rods, transmission shafts). Lowest application temp. -40 °C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.8 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

9 - 11 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Nickel Chromium Molybdenum Steel

Reduction of area

20.0 °C

40 - 50 %

Tensile strength

20.0 °C

1000 - 1400 MPa

Yield strength

20.0 °C

800 - 1000 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.21E-5 1/K

200.0 °C

1.27E-5 1/K

300.0 °C

1.32E-5 1/K

400.0 °C

1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Max service temperature, long

-40 - 0 °C

Melting point

1382 - 1529 °C

Typical for Nickel Chromium Molybdenum Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

33.7 W/(m·K)

100.0 °C

36.2 W/(m·K)

200.0 °C

37.8 W/(m·K)

300.0 °C

37.2 W/(m·K)

400.0 °C

35.7 W/(m·K)

500.0 °C

34 W/(m·K)

600.0 °C

32 W/(m·K)

Thermal diffusivity

20.0 °C

9.4 mm²/s

100.0 °C

9.4 mm²/s

200.0 °C

9.2 mm²/s

300.0 °C

8.5 mm²/s

400.0 °C

7.6 mm²/s

500.0 °C

6.6 mm²/s

600.0 °C

5.4 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

3.09E-7 Ω·m

100.0 °C

3.54E-7 Ω·m

200.0 °C

4.18E-7 Ω·m

300.0 °C

5.05E-7 Ω·m

400.0 °C

6.09E-7 Ω·m

500.0 °C

7.27E-7 Ω·m

600.0 °C

8.67E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.3 - 0.38 %

Chromium

1.4 - 1.7 %

Manganese

0.4 - 0.7 %

Molybdenum

0.15 - 0.3 %

Nickel

1.4 - 1.7 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.03 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10277-5 Grade 34CrNiMo6 Quenched, Tempered, and Cold‑Drawn Steel (+QT+C) – High‑Strength, Low‑Temperature Performance
    2. Grade 34CrNiMo6 Cold Drawn, Quenched & Tempered Steel – EN 10277‑5
    3. High-Strength 25CrMo4 Steel – EN 10277-5 Cold-Drawn, Turned, Quenched & Tempered
    4. EN 10277‑5: 25CrMoS4 Cold‑Drawn, Quenched & Tempered – Premium High‑Strength Steel for Automotive & Engine Parts
    5. EN 10277-5 Grade 28Cr4: High‑Strength Cold Drawn or Turned Steel, Quenched and Tempered
    6. EN 10277-5 Grade 34CrS4 Cold-Drawn or Turned Steel – Quenched & Tempered for Vehicle and Engine Applications
    7. EN 10277-5 Grade 36CrNiMo4 – Cold-Drawn, Turned, Quenched & Tempered Steel for High-Performance Applications
    8. EN 10277-5 Grade 37Cr4: Premium Cold-Drawn & Quenched Steel for High-Performance Automotive & Machine Parts
    9. EN 10277-5 Grade 37CrS4: High-Performance Cold-Drawn, Quenched, and Tempered Steel for Automotive & Machinery Applications
    10. EN 10277-5 Grade 38Cr2 – Cold‑Drawn, Quenched & Tempered Steel for High‑Strength Automotive Components