High-Strength 25CrMo4 Steel – EN 10277-5 Cold-Drawn, Turned, Quenched & Tempered

Steel 25 CrMo 4 is suitable for parts of high strength and ductility requirements and mean and higher heat-treatment sections in vehicle manufacturing, engine and machine engineering (e.g. crankshafts, steering knuckles, pinions). Lowest application temp. -40 °C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.83 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

12 - 15 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Chromium Molybdenum Steel

Reduction of area

20.0 °C

50 - 60 %

Tensile strength

20.0 °C

700 - 1100 MPa

Yield strength

20.0 °C

450 - 700 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.21E-5 1/K

200.0 °C

1.27E-5 1/K

300.0 °C

1.32E-5 1/K

400.0 °C

1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Max service temperature, long

-40 - 200 °C

Melting point

1382 - 1529 °C

Typical for Chromium Molybdenum Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

41 W/(m·K)

100.0 °C

42.7 W/(m·K)

200.0 °C

42.8 W/(m·K)

300.0 °C

41.6 W/(m·K)

400.0 °C

39.9 W/(m·K)

500.0 °C

37.8 W/(m·K)

600.0 °C

35.6 W/(m·K)

Thermal diffusivity

20.0 °C

11.4 mm²/s

100.0 °C

11 mm²/s

200.0 °C

10.3 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.5 mm²/s

500.0 °C

7.3 mm²/s

600.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

2.54E-7 Ω·m

100.0 °C

3E-7 Ω·m

200.0 °C

3.69E-7 Ω·m

300.0 °C

4.51E-7 Ω·m

400.0 °C

5.45E-7 Ω·m

500.0 °C

6.54E-7 Ω·m

600.0 °C

7.78E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.22 - 0.29 %

Chromium

0.9 - 1.2 %

Manganese

0.6 - 0.9 %

Molybdenum

0.15 - 0.3 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.03 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10277‑5: 25CrMoS4 Cold‑Drawn, Quenched & Tempered – Premium High‑Strength Steel for Automotive & Engine Parts
    2. EN 10277-5 Grade 28Cr4: High‑Strength Cold Drawn or Turned Steel, Quenched and Tempered
    3. EN 10277-5 Grade 34CrS4 Cold-Drawn or Turned Steel – Quenched & Tempered for Vehicle and Engine Applications
    4. EN 10277-5 Grade 36CrNiMo4 – Cold-Drawn, Turned, Quenched & Tempered Steel for High-Performance Applications
    5. EN 10277-5 Grade 37Cr4: Premium Cold-Drawn & Quenched Steel for High-Performance Automotive & Machine Parts
    6. EN 10277-5 Grade 37CrS4: High-Performance Cold-Drawn, Quenched, and Tempered Steel for Automotive & Machinery Applications
    7. EN 10277-5 Grade 38Cr2 – Cold‑Drawn, Quenched & Tempered Steel for High‑Strength Automotive Components
    8. EN 10277-5 Grade 38CrS2: High-Strength Cold-Drawn, Turned, Quenched & Tempered Steel
    9. EN 10277‑5 Grade 41Cr4 Steel – Cold‑Drawn, Turned, Quenched & Tempered
    10. EN 10277-5 Grade 41CrS4: High‑Strength Cold‑Drawn Steel for Automotive and Machinery Applications