AW-2017A Aluminium Grade (O3) – EN 573-3 Standard Specifications
Properties
General
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Density | 2.8 g/cm³ | O3 | EN 573-3, EN 1715-3 | Strip, Sheet, Plate, Tube, Bar |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 72.5 GPa | O3 | EN 573-3, EN 1715-3 | Strip, Sheet, Plate, Tube, Bar | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Shear modulus | 27.2 GPa | O3 | EN 573-3, EN 1715-3 | Strip, Sheet, Plate, Tube, Bar | |
Tensile strength | 150.0 - 220.0 MPa | O3 | EN 573-3, EN 1715-3 | Strip, Sheet, Plate, Tube, Bar |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3e-05 1/K | O3 | EN 573-3, EN 1715-3 | Strip, Sheet, Plate, Tube, Bar | |
100 °C | 2.3e-05 1/K | O3 | EN 573-3, EN 1715-3 | Strip, Sheet, Plate, Tube, Bar | ||
Melting point | 512.0 - 650.0 °C | O3 | EN 573-3, EN 1715-3 | Strip, Sheet, Plate, Tube, Bar | ||
Specific heat capacity | 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium | ||||
Thermal conductivity | 130.0 - 200.0 W/(m·K) | O3 | EN 573-3, EN 1715-3 | Strip, Sheet, Plate, Tube, Bar |
Electrical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Electrical conductivity | 18000000.0 - 28000000.0 S/m | O3 | EN 573-3, EN 1715-3 | Strip, Sheet, Plate, Tube, Bar |
Electrical resistivity | 3.57e-08 - 5.56e-08 Ω·m | O3 | EN 573-3, EN 1715-3 | Strip, Sheet, Plate, Tube, Bar |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.1 % | O3 | EN 573-3, EN 1715-3 | Strip, Sheet, Plate, Tube, Bar |
Copper | 3.5 - 4.5 % | O3 | EN 573-3, EN 1715-3 | Strip, Sheet, Plate, Tube, Bar |
Iron | 0.70 % | O3 | EN 573-3, EN 1715-3 | Strip, Sheet, Plate, Tube, Bar |
Magnesium | 0.4 - 1.0 % | O3 | EN 573-3, EN 1715-3 | Strip, Sheet, Plate, Tube, Bar |
Manganese | 0.4 - 1.0 % | O3 | EN 573-3, EN 1715-3 | Strip, Sheet, Plate, Tube, Bar |
Silicon | 0.2 - 0.8 % | O3 | EN 573-3, EN 1715-3 | Strip, Sheet, Plate, Tube, Bar |
Zinc | 0.25 % | O3 | EN 573-3, EN 1715-3 | Strip, Sheet, Plate, Tube, Bar |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: not suitable, Protective: good | |
| Brazing | hard brazing (with flux/ without flux): not suitable / not suitable, friction soldering: acceptable, soft brazing with flux: not suitable | |
| Corrosion properties | Seawater: poor, weathering: sufficient | |
| Workability | Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) acceptable (O) / acceptable (O) | |
Metal
- AW-2017A F Aluminium Alloy – EN 573-3 Grade Specification
- AW-2017A H18: EN 573-3 Grade AlCu Age-Hardenable Alloy
- EN 573-3 Grade AW-2017A H13 – High-Strength Age-Hardenable Aluminum‑Copper Alloy
- EN 573-3 AW‑2017A T3 Aluminum Alloy – Technical Specifications
- EN 573-3 AW-2017A T351: Premium Age-Hardenable AlCu Alloy
- EN 573-3 AW-2017A T3510: High-Performance Age-Hardenable AlCu Alloy
- EN 573-3 Grade AW‑2017A (T3511) – High‑Strength Age‑Hardening Al‑Cu Alloy
- AW-2017A H111 – EN 573‑3 Grade Age‑Hardenable AlCu Alloy
- EN 573-3 AW-2017A T4510 Aluminum Alloy – Specifications & Properties
- EN 573-3 AW-2017A T4511: High-Performance Age-Hardenable AlCu Alloy