EN 573-3 Grade AW-2017A H13 – High-Strength Age-Hardenable Aluminum‑Copper Alloy

Age-hardenable AlCu alloy. The alloy is not food safe.

Properties

General

Property	Temperature	Value	Condition	Related Standards	Shape
Density		2.8 g/cm³	H13	EN 573-3, EN 1301	Strip, Sheet, Plate, Tube, Bar
	20.0 °C	2.8 g/cm³	H13	EN 573-3	Wire

Mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Elastic modulus		72.5 GPa	H13	EN 573-3, EN 1301	Strip, Sheet, Plate, Tube, Bar
	20.0 °C	65.0 - 73.5 GPa	H13	EN 573-3	Wire
Elongation		5.0 %	H13	EN 573-3, EN 1301	Strip, Sheet, Plate, Tube, Bar
	20.0 °C	5.0 %	H13	EN 573-3	Wire	A100
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m				Typical for Wrought 2000 Series Aluminium
Poisson's ratio		0.33 [-]				Typical for Wrought 2000 Series Aluminium
Shear modulus		27.2 GPa	H13	EN 573-3, EN 1301	Strip, Sheet, Plate, Tube, Bar
	20.0 °C	26.0 - 28.5 GPa	H13	EN 573-3	Wire
Tensile strength	20.0 °C	210.0 - 300.0 MPa	H13	EN 573-3, EN 1301	Wire, Strip, Sheet, Plate, Tube, Bar

Thermal

Property	Temperature	Value	Condition	Related Standards	Shape
Coefficient of thermal expansion	20 °C	2.3e-05 1/K	H13	EN 573-3, EN 1301	Strip, Sheet, Plate, Tube, Bar
	100 °C	2.3e-05 1/K	H13	EN 573-3, EN 1301	Strip, Sheet, Plate, Tube, Bar
Melting point		512.0 - 650.0 °C	H13	EN 573-3, EN 1301	Strip, Sheet, Plate, Tube, Bar
Specific heat capacity	20.0 °C	921.0 J/(kg·K)	H13	EN 573-3	Wire
Thermal conductivity	20.0 °C	130.0 - 200.0 W/(m·K)	H13	EN 573-3, EN 1301	Wire, Strip, Sheet, Plate, Tube, Bar

Electrical

Property	Temperature	Value	Condition	Related Standards	Shape
Electrical conductivity	20.0 °C	18000000.0 - 28000000.0 S/m	H13	EN 573-3, EN 1301	Wire, Strip, Sheet, Plate, Tube, Bar
Electrical resistivity		3.57e-08 - 5.56e-08 Ω·m	H13	EN 573-3, EN 1301	Strip, Sheet, Plate, Tube, Bar

Chemical properties

Property	Value	Condition	Related Standards	Shape
Chromium	0.1 %	H13	EN 573-3, EN 1301	Wire, Strip, Sheet, Plate, Tube, Bar
Copper	3.5 - 4.5 %	H13	EN 573-3, EN 1301	Wire, Strip, Sheet, Plate, Tube, Bar
Iron	0.7 %	H13	EN 573-3	Wire
	0.70 %	H13	EN 573-3, EN 1301	Strip, Sheet, Plate, Tube, Bar
Magnesium	0.4 - 1.0 %	H13	EN 573-3, EN 1301	Wire, Strip, Sheet, Plate, Tube, Bar
Manganese	0.4 - 1.0 %	H13	EN 573-3, EN 1301	Wire, Strip, Sheet, Plate, Tube, Bar
Silicon	0.2 - 0.8 %	H13	EN 573-3, EN 1301	Wire, Strip, Sheet, Plate, Tube, Bar
Zinc	0.25 %	H13	EN 573-3, EN 1301	Wire, Strip, Sheet, Plate, Tube, Bar

Technological properties

Property
Anodizing	decorative: not suitable, Protective: good
Brazing	hard brazing (with flux/ without flux): not suitable / not suitable, friction soldering: acceptable, soft brazing with flux: not suitable
Corrosion properties	Seawater: poor, weathering: sufficient
Workability	Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) acceptable (O) / acceptable (O)