EN 573-3 Grade AW-1350 H112 Aluminum Alloy – High‑Quality Wire & Extrusion Material

Material EN AW-EAl 99,5 is produced in high amount for wire and prewire for electrotechnical applications as well as for extruded components and drawn parts. The alloy is food-safe.

Properties

General

Property	Value	Condition	Related Standards	Shape
Density	2.7 g/cm³	H112	EN 573-3, EN 485, EN 755	Plate, Rod
	2.705 g/cm³	H112	EN 573-3, EN 485, EN 755	Plate, Rod

Mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Elastic modulus		69.0 GPa	H112	EN 573-3, EN 485, EN 755	Plate, Rod
		70.0 GPa	H112	EN 573-3, EN 485, EN 755	Plate, Rod
Elongation		20.0 %	H112	EN 573-3, EN 485	Plate, Rod	A50
		20.0 %	H112	EN 573-3, EN 485	Plate, Rod
		23.0 %	H112	EN 573-3, EN 755	Plate, Rod	A50
		25.0 %	H112	EN 573-3, EN 755	Plate, Rod	A100
	20.0 °C	23.0 %	H112	EN 573-3	Profile, Rod, Tube	A50
	20.0 °C	25.0 %	H112	EN 573-3	Profile, Rod, Tube
Hardness, Brinell		23.0 [-]	H112	EN 573-3, EN 485	Plate, Rod
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m				Typical for Wrought 1000 Series Aluminium
Poisson's ratio		0.33 [-]				Typical for Wrought 1000 Series Aluminium
Shear modulus		25.9 GPa				Typical for Wrought 1000 Series Aluminium
Tensile strength		60.0 MPa	H112	EN 573-3, EN 755	Plate, Rod
		75.0 MPa	H112	EN 573-3, EN 485	Plate, Rod
	20.0 °C	60.0 MPa	H112	EN 573-3	Profile, Rod, Tube

Thermal

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coefficient of thermal expansion	20 °C	2.36e-05 1/K	H112	EN 573-3, EN 485, EN 755	Plate, Rod
	20 °C	2.38e-05 1/K	H112	EN 573-3, EN 485, EN 755	Plate, Rod
	100 °C	2.36e-05 1/K	H112	EN 573-3, EN 485, EN 755	Plate, Rod
	100 °C	2.38e-05 1/K	H112	EN 573-3, EN 485, EN 755	Plate, Rod
Melting point		645.0 - 657.0 °C	H112	EN 573-3, EN 485, EN 755	Plate, Rod
		645.0 - 655.0 °C	H112	EN 573-3, EN 485, EN 755	Plate, Rod
Specific heat capacity		900.0 - 963.0 J/(kg·K)				Typical for Wrought 1000 Series Aluminium
Thermal conductivity		225.0 - 235.0 W/(m·K)	H112	EN 573-3, EN 485, EN 755	Plate, Rod
		234 W/(m·K)	H112	EN 573-3, EN 485, EN 755	Plate, Rod

Electrical

Property	Value	Condition	Related Standards	Shape
Electrical conductivity	35400000.0 - 36500000.0 S/m	H112	EN 573-3, EN 485, EN 755	Plate, Rod
	36000000.0 S/m	H112	EN 573-3, EN 485, EN 755	Plate, Rod
Electrical resistivity	2.74e-08 - 2.82e-08 Ω·m	H112	EN 573-3, EN 485, EN 755	Plate, Rod
	2.78e-08 Ω·m	H112	EN 573-3, EN 485, EN 755	Plate, Rod

Chemical properties

Property	Value	Condition	Related Standards	Shape
Aluminium	99.5 %	H112	EN 573-3, EN 485, EN 755	Plate, Rod
Boron	0.05 %	H112	EN 573-3, EN 485, EN 755	Plate, Rod, Profile, Tube
Chromium	0.01 %	H112	EN 573-3, EN 485, EN 755	Plate, Rod, Profile, Tube
Copper	0.05 %	H112	EN 573-3, EN 485, EN 755	Plate, Rod, Profile, Tube
Gallium	0.03 %	H112	EN 573-3, EN 485, EN 755	Plate, Rod, Profile, Tube
Iron	0.40 %	H112	EN 573-3, EN 485, EN 755	Plate, Rod
	0.4 %	H112	EN 573-3	Profile, Rod, Tube
Manganese	0.01 %	H112	EN 573-3, EN 485, EN 755	Plate, Rod, Profile, Tube
Silicon	0.1 %	H112	EN 573-3, EN 485, EN 755	Plate, Rod, Profile, Tube
Zinc	0.05 %	H112	EN 573-3, EN 485, EN 755	Plate, Rod, Profile, Tube

Technological properties

Property
Brazing	Excellent
Workability	Excellent workability.

Property

Brazing

Excellent

Workability

Excellent workability.