EN 573-3 AW-5005A H112 – Food‑Safe Aluminum‑Magnesium Alloy
Naturally hard AlMg alloy. The alloy is food safe.
Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 2.69 g/cm³ | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar | |
20.0 °C | 2.69 g/cm³ | H112 | EN 573-3 | Profile, Rod, Tube | |
20.0 °C | 2.69 - 2.7 g/cm³ | H112 | EN 573-3 | Profile, Rod, Tube | |
20.0 °C | 2.7 g/cm³ | H112 | EN 573-3 | Profile, Rod, Tube |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 69.5 GPa | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar | ||
20.0 °C | 69.5 GPa | H112 | EN 573-3 | Profile, Rod, Tube | ||
Elongation | 16.0 % | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar | A50 | |
18.0 % | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar | A100 | ||
20.0 °C | 16.0 % | H112 | EN 573-3 | Profile, Tube, Rod | A50 | |
20.0 °C | 18.0 % | H112 | EN 573-3 | Profile, Tube, Rod | ||
Hardness, Brinell | 20.0 °C | 30.0 [-] | H112 | EN 573-3 | Profile, Tube, Rod | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||||
Poisson's ratio | 20.0 °C | 0.33 [-] | H112 | EN 573-3 | Profile, Rod, Tube | |
Shear modulus | 26.1 GPa | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar | ||
20.0 °C | 25.0 - 26.1 GPa | H112 | EN 573-3 | Profile, Rod, Tube | ||
20.0 °C | 26.1 GPa | H112 | EN 573-3 | Profile, Rod, Tube | ||
Tensile strength | 100.0 MPa | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar | ||
20.0 °C | 100.0 MPa | H112 | EN 573-3 | Profile, Tube, Rod |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | -50 °C | 2.18e-05 1/K | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar, Profile, Rod | |
-50.0 °C | 2.18e-05 1/K | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar, Profile, Rod | ||
20 °C | 2.18e-05 1/K | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar, Profile, Rod | ||
20 °C | 2.36e-05 1/K | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar, Profile, Rod | ||
20 °C | 2.45e-05 1/K | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar, Profile, Rod | ||
20 °C | 2.55e-05 1/K | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar, Profile, Rod | ||
100 °C | 2.36e-05 1/K | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar, Profile, Rod | ||
100.0 °C | 2.36e-05 1/K | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar, Profile, Rod | ||
200 °C | 2.45e-05 1/K | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar, Profile, Rod | ||
200.0 °C | 2.45e-05 1/K | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar, Profile, Rod | ||
300 °C | 2.55e-05 1/K | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar, Profile, Rod | ||
300.0 °C | 2.55e-05 1/K | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar, Profile, Rod | ||
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium | ||||
Melting point | 630.0 - 650.0 °C | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar | ||
Specific heat capacity | 20.0 °C | 879.0 J/(kg·K) | H112 | EN 573-3 | Profile, Rod, Tube | |
20.0 °C | 879.0 - 899.0 J/(kg·K) | H112 | EN 573-3 | Profile, Rod, Tube | ||
20.0 °C | 899.0 J/(kg·K) | H112 | EN 573-3 | Profile, Rod, Tube | ||
Thermal conductivity | 20.0 °C | 160.0 - 220.0 W/(m·K) | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar, Profile, Rod | |
20.0 °C | 160.0 - 201.0 W/(m·K) | H112 | EN 573-3 | Profile, Rod, Tube | ||
20.0 °C | 201.0 - 220.0 W/(m·K) | H112 | EN 573-3 | Profile, Rod, Tube | ||
20.0 °C | 201.0 W/(m·K) | H112 | EN 573-3 | Profile, Rod, Tube |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 23000000.0 - 31000000.0 S/m | H112 | EN 573-3, EN 755 | Profile, Rod, Tube, Strip, Sheet, Plate, Bar |
Electrical resistivity | 3.23e-08 - 4.35e-08 Ω·m | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar | |
20.0 °C | 3.3e-08 Ω·m | H112 | EN 573-3 | Profile, Rod, Tube |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.1 % | H112 | EN 573-3, EN 755 | Profile, Rod, Tube, Strip, Sheet, Plate, Bar |
Copper | 0.05 % | H112 | EN 573-3, EN 755 | Profile, Rod, Tube, Strip, Sheet, Plate, Bar |
Iron | 0.45 % | H112 | EN 573-3 | Profile, Rod, Tube |
0.45 % | H112 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar | |
Magnesium | 0.7 - 1.1 % | H112 | EN 573-3, EN 755 | Profile, Rod, Tube, Strip, Sheet, Plate, Bar |
Manganese | 0.15 % | H112 | EN 573-3, EN 755 | Profile, Rod, Tube, Strip, Sheet, Plate, Bar |
Silicon | 0.3 % | H112 | EN 573-3, EN 755 | Profile, Rod, Tube, Strip, Sheet, Plate, Bar |
Zinc | 0.2 % | H112 | EN 573-3, EN 755 | Profile, Rod, Tube, Strip, Sheet, Plate, Bar |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: gut (EQ: sehr gut), Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): sufficient - poor / sufficient, friction soldering: good, soft brazing with flux: acceptable | |
| Corrosion properties | Seawater: good, weathering: very good | |
| Workability | Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / good (H12) | |
Metal
- EN 573-3 Grade 3.3315 H112 – Comprehensive Material Specifications
- EN 573-3 Grade 3.3326 H112 Aluminium – Density, Modulus, Strength & Standards
- EN 573-3 Grade 3.0285 H112: Comprehensive Material Properties
- EN 573-3 Grade 3.0515 H112 Aluminium – Key Properties & Standards
- EN 573-3 Grade 3.3316 H112: Detailed Material Properties & Standards
- EN 573-3 Grade 3.0257 H112 – Comprehensive Aluminium Alloy Properties
- EN 573-3 Grade 3.0275 H112 – Premium Steel for Advanced Applications
- EN 573-3 Grade 3.3555 H112 – Aluminium Alloy Specifications & Key Properties
- EN 573-3 Grade 3.3525 H112 Aluminium: Properties & Standards
- EN 573-3 Grade 3.0205 H112 – Detailed Properties & Standards