EN 573-3 Grade 3.0275 H112 – Premium Steel for Advanced Applications
Quantity: One truck load – Specialty products on request.Additional services: Via Cindal (the Aludium R&D department): R&D services, benchmarking, chemical audits, material specification, process optimisation, quality monitoring, sample analysis, prototyping, training
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.7 g/cm³ | H112 | EN 573-3, EN 485, EN 755 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 70.0 GPa | H112 | EN 573-3, EN 485, EN 755 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 1000 Series Aluminium | ||
Shear modulus | 25.9 GPa | Typical for Wrought 1000 Series Aluminium | ||
Tensile strength | 60.0 MPa | H112 | EN 573-3, EN 755 | |
70.0 MPa | H112 | EN 573-3, EN 485 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.35e-05 1/K | H112 | EN 573-3, EN 485, EN 755 | |
100 °C | 2.35e-05 1/K | H112 | EN 573-3, EN 485, EN 755 | ||
Melting point | 659.0 °C | H112 | EN 573-3, EN 485, EN 755 | ||
Specific heat capacity | 900.0 - 963.0 J/(kg·K) | Typical for Wrought 1000 Series Aluminium | |||
Thermal conductivity | 225 W/(m·K) | H112 | EN 573-3, EN 485, EN 755 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 34500000.0 - 35000000.0 S/m | H112 | EN 573-3, EN 485, EN 755 |
Electrical resistivity | 2.86e-08 - 2.9e-08 Ω·m | H112 | EN 573-3, EN 485, EN 755 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 99.7 % | H112 | EN 573-3, EN 485, EN 755 |
Copper | 0.03 % | H112 | EN 573-3, EN 485, EN 755 |
Iron | 0.25 % | H112 | EN 573-3, EN 485, EN 755 |
Magnesium | 0.03 % | H112 | EN 573-3, EN 485, EN 755 |
Manganese | 0.03 % | H112 | EN 573-3, EN 485, EN 755 |
Silicon | 0.2 % | H112 | EN 573-3, EN 485, EN 755 |
Titanium | 0.03 % | H112 | EN 573-3, EN 485, EN 755 |
Zinc | 0.07 % | H112 | EN 573-3, EN 485, EN 755 |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: very good, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): very good / very good, friction soldering: very good, soft brazing with flux: very good | |
| Workability | Bending / Spinning (cold): very good / very good, Impact extrusion (cold): very good, Deep drawing / upsetting (Condition) very good (H14) / very good (H12) | |
Metal
- EN 573-3 Grade 3.3315 H112 – Comprehensive Material Specifications
- EN 573-3 Grade 3.3326 H112 Aluminium – Density, Modulus, Strength & Standards
- EN 573-3 Grade 3.0285 H112: Comprehensive Material Properties
- EN 573-3 Grade 3.0515 H112 Aluminium – Key Properties & Standards
- EN 573-3 Grade 3.3316 H112: Detailed Material Properties & Standards
- EN 573-3 Grade 3.0257 H112 – Comprehensive Aluminium Alloy Properties
- EN 573-3 Grade 3.0275 – High-Performance Aluminium Alloy for Structural Applications
- EN 573-3 Grade 3.0275 H26 – High-Strength Steel with R&D Support
- EN 573-3 Grade 3.3555 H112 – Aluminium Alloy Specifications & Key Properties
- EN 573-3 Grade 3.3525 H112 Aluminium: Properties & Standards