EN 1706 Grade AC-48100 F Aluminium Casting Alloy – Key Properties & Standards
Aluminium casting alloy (pressure die casting, investment casting)
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.65 - 2.7 g/cm³ | Typical for Cast 3xx.x Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 60.0 - 90.0 MPa | F | EN 1706 | Casting | |
Elastic modulus | 73.0 - 80.0 GPa | Typical for Cast 3xx.x Series Aluminium | |||
Hardness, Brinell | 90.0 [-] | F | EN 1706 | Casting | |
Poisson's ratio | 0.33 [-] | Typical for Cast 3xx.x Series Aluminium | |||
Shear modulus | 2.8 GPa | Typical for Cast 3xx.x Series Aluminium | |||
Tensile strength | 200.0 MPa | F | EN 1706 | Casting | |
220.0 MPa | F | EN 1706 | Casting |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 1.8e-05 1/K | F | EN 1706 | Casting | |
100 °C | 1.8e-05 1/K | F | EN 1706 | Casting | ||
Melting point | 505.0 - 770.0 °C | Typical for Cast 3xx.x Series Aluminium | ||||
Specific heat capacity | 960.0 - 963.0 J/(kg·K) | Typical for Cast 3xx.x Series Aluminium | ||||
Thermal conductivity | 120.0 - 130.0 W/(m·K) | F | EN 1706 | Casting |
Electrical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Electrical conductivity | 14000000.0 - 17000000.0 S/m | F | EN 1706 | Casting |
Electrical resistivity | 5.88e-08 - 7.14e-08 Ω·m | F | EN 1706 | Casting |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Aluminium | 71.95 % | F | EN 1706 | |
Copper | 4.0 - 5.0 % | F | EN 1706 | Casting |
Iron | 1.3 % | F | EN 1706 | |
1.3 % | F | EN 1706 | Casting | |
Magnesium | 0.25 - 0.65 % | F | EN 1706 | Casting |
Manganese | 0.5 % | F | EN 1706 | Casting |
Nickel | 0.3 % | F | EN 1706 | Casting |
Silicon | 16.0 - 18.0 % | F | EN 1706 | Casting |
Tin | 0.15 % | F | EN 1706 | Casting |
Titanium | 0.25 % | F | EN 1706 | Casting |
Zinc | 1.5 % | F | EN 1706 | Casting |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: not sufficient | |
| Corrosion properties | general: not sufficient | |
| General machinability | after thermal treatment: good, as cast: not recommended | |
| Processing methods | investment casting, separately cast test sample | |
Metal
- EN 1706 AC-44000 F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 Grade AC-44100 F – High-Performance Aluminium Casting Alloy
- EN 1706 Grade AC-44200 F Aluminium Casting Alloy – High-Performance, Industrial Grade
- EN 1706 AC-44300 F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 AC-44400F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 AC-48100 T5 Aluminium Alloy – Specifications & Properties
- EN 1706 AC-51200 F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 Grade AC-51300 F – High-Strength Aluminium Casting Alloy
- EN 1706 AC-46500 F – Aluminium Die Casting Alloy: Properties & Standards
- EN 1706 AC‑46600 F Aluminium Alloy – High‑Strength, Low‑Density Casting Solution