JIS H4040 2017 Grade T4 Aluminum Alloy – Heat‑Treatable, Strong, and Machinable
Aluminum JIS 2017 is a heat treatable wrought alloy that offers decent strength, ductility, and good machinability. Aluminum JIS 2017 offers more strength than Aluminum 2011, and has fair workability and corrosion resistance. As with many aluminum alloys, Aluminum JIS 2017 should not be welded as it reduces the alloy’s corrosion resistance.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.75 - 2.84 g/cm³ | Typical for Wrought 2000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 70.0 - 73.0 GPa | Typical for Wrought 2000 Series Aluminium | ||
Elongation | 12.0 % | T4 | JIS H4040 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||
Shear modulus | 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | ||
Tensile strength | 343.0 MPa | T4 | JIS H4040 | |
Yield strength | 216.0 MPa | T4 | JIS H4040 |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium |
Melting point | 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium |
Specific heat capacity | 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium |
Thermal conductivity | 112.0 - 251.0 W/(m·K) | Typical for Wrought 2000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Technological properties
| Property | ||
|---|---|---|
| Processing history | T4 | |
| Workability | Moderate Workability | |
Metal
- Aluminum JIS 2017 – Grade 2017 O: Heat‑Treatable, Strong & Corrosion‑Resistant Alloy
- JIS H4040 Grade 3003 Aluminum Alloy – Superior Corrosion Resistance & Weldability
- JIS H4040 5052 Aluminum Alloy – Superior Corrosion Resistance & Weldability
- JIS H4120 Grade 2017 T4 Aluminum Alloy – High Strength & Machinability
- JIS H4140 2017 T4 Aluminum Alloy – Superior Strength & Machinability
- JIS H4040 Grade 7075 O – Premium Aerospace-Grade Aluminum Alloy
- JIS H4040 Grade 7075 T6 – High‑Strength Aluminum Alloy for Aerospace Applications
- JIS H4080 Grade 2017 O – High-Performance Heat-Treatable Aluminum Alloy
- JIS H4080 Grade 2017 T4 – Premium Heat‑Treatable Aluminum Alloy
- JIS H4040 Grade 2017O: Heat‑Treatable Aluminum Alloy with Superior Strength & Machinability