JIS H4040 2024 T4 Aluminum Alloy – High Strength for Aerospace Applications
Aluminum JIS 2024, known for its use in aircraft industry, is an alloy that offers excellent strength. When in the annealed condition it is readily formed and has good machinability. Though it has a relatively low level of corrosion resistance, it can be machined to a high finish.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.75 - 2.84 g/cm³ | Typical for Wrought 2000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 70.0 - 73.0 GPa | Typical for Wrought 2000 Series Aluminium | ||
Elongation | 12.0 % | T4 | JIS H4040 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||
Shear modulus | 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | ||
Tensile strength | 392.0 MPa | T4 | JIS H4040 | |
Yield strength | 294.0 MPa | T4 | JIS H4040 |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium |
Melting point | 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium |
Specific heat capacity | 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium |
Thermal conductivity | 112.0 - 251.0 W/(m·K) | Typical for Wrought 2000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Technological properties
| Property | ||
|---|---|---|
| Processing history | T4 | |
| Workability | Moderate Workability | |
Metal
- JIS H4040 Grade 5056 Aluminium – Technical Overview
- JIS H4040 Grade 7N01 T4 – Premium 7000 Series Aluminium Alloy
- JIS H4040 7N01 T6 Aluminium – Detailed Specs & Engineering Properties
- JIS H4040 Grade 5056 O Aluminum – Premium 5000 Series Material
- JIS H4040 Grade 5083 O – 5000 Series Aluminum Alloy Specification
- JIS H4040 Grade 2011 T3 – Premium Aluminum Alloy for Precision Machining
- JIS H4100 2024-O Aluminum Alloy – High Strength, Aircraft‑Grade Performance
- 2024 T4 Aluminum (JIS H4100) – High Strength, Aerospace‑Grade, Machinable Alloy
- 2024-T4 Aluminum (JIS H4080) – Aircraft-Grade, High-Strength Alloy
- JIS H4040 Grade 2024 O Aluminum Alloy: High Strength & Machinability