EN 10277-5 Grade C50E Cold Drawn Steel – High Strength for Heavy Engineering

Steel C50E is suitable for larger parts (heavy forged parts) in vehicle, engine and machine engineering (e.g. transmission parts, shafts, wheel hubs). Lowest application temperature -25°C. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.8 - 7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

205 - 207 GPa

200.0 °C

195 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

175 - 184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

5 - 8 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Medium Carbon Steel

Shear modulus

20.0 °C

81 GPa

Tensile strength

20.0 °C

650 - 1100 MPa

Yield strength Rp0.2

20.0 °C

390 - 590 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.11E-5 - 1.25E-5 1/K

200.0 °C

1.21E-5 - 1.3E-5 1/K

300.0 °C

1.29E-5 - 1.36E-5 1/K

400.0 °C

1.35E-5 - 1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Max service temperature, long

-25 - 0 °C

Melting point

1380 - 1514 °C

Typical for Medium Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

460 - 461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

41.7 - 52 W/(m·K)

100.0 °C

43.4 - 50.6 W/(m·K)

200.0 °C

43.2 - 48.1 W/(m·K)

300.0 °C

41.4 - 45.7 W/(m·K)

400.0 °C

39.1 W/(m·K)

500.0 °C

36.7 W/(m·K)

600.0 °C

34.1 W/(m·K)

Thermal diffusivity

20.0 °C

11.6 mm²/s

100.0 °C

11.3 mm²/s

200.0 °C

10.5 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.3 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.2E-7 - 2.5E-7 Ω·m

100.0 °C

2.95E-7 Ω·m

200.0 °C

3.65E-7 Ω·m

300.0 °C

4.53E-7 Ω·m

400.0 °C

5.56E-7 Ω·m

500.0 °C

6.74E-7 Ω·m

600.0 °C

8.13E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.47 - 0.55 %

Chromium

0.4 %

Manganese

0.6 - 0.9 %

Molybdenum

0.1 %

Nickel

0.4 %

Phosphorus

0.03 - 0.04 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10277-5 Grade 25CrMo4 Cold-Drawn Steel – High Strength & Ductility
    2. EN 10277-5 Grade 25CrMoS4 Cold-Drawn Steel – High Strength & Ductility for Automotive & Industrial Applications
    3. EN 10277-5 Grade 38Cr2 Cold Drawn Steel – High Strength & Low-Temperature Performance
    4. EN 10277-5 Grade 38CrS2 Cold Drawn Steel – Precision Alloy for Automotive and Machinery
    5. EN 10277‑5 Grade 41Cr4 Cold‑Drawn Steel – High‑Performance for Automotive & Machine Engineering
    6. EN 10277-5 Grade 41CrS4 Cold-Drawn Steel – High Strength for Automotive and Industrial Applications
    7. EN 10277-5 Grade 42CrMo4 – Premium Cold‑Drawn Steel for Heavy‑Duty Applications
    8. EN 10277‑5 Grade 46Cr2 Cold‑Drawn Steel – High Strength, Low Ductility for Vehicle Components
    9. EN 10277-5 Grade 46CrS2 Cold Drawn Steel – High Strength & Workability
    10. EN 10277-5 Grade 50CrMo4 Cold Drawn Steel – High‑Strength, Low‑Temperature Performance