EN 12164 Grade CuZn39Pb0.5 (R410) – Unhardenable Wrought Brass with Enhanced Machinability
Material CuZn39Pb0,5, mat. No. CW610N, is an unhardenable wrought alloy. to the comparable make CuZn39Pb0,5, mat. No. 2.0372 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for the unleaded brass grade of the same Zn-content. Machinability is improved by Pb-addition. Corrosion resistance to water, several saline solutions and organic liquids is also lower than for unleaded alloys of the same zinc-content. Processing properties: warm forming: very good cold forming: moderately machinability: good hard soldering: moderately soft soldering: very good TIG-welding: moderately burnishing: very good Application: For plug pins, fitting parts, rivets, condenser plates, floor plate screeding and drawing instruments.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.4 g/cm³ |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 20.0 °C | 102 GPa |
Elongation | 20.0 °C | 12 - 15 % |
Elongation A10 | 20.0 °C | 12 % |
Elongation A100 | 20.0 °C | 8 - 10 % |
Elongation A11.3 | 20.0 °C | 10 % |
Shear modulus | 20.0 °C | 37 GPa |
Tensile strength | 20.0 °C | 410 MPa |
Yield strength Rp0.2 | 20.0 °C | 190 - 250 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 200.0 °C | 2.04E-5 1/K | |
Melting point | 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 23.0 °C | 371 - 418 J/(kg·K) | Typical for Wrought Copper Brass |
Thermal conductivity | 20.0 °C | 109 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 1.39E+7 S/m |
Electrical resistivity | 20.0 °C | 7.2E-8 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 0.05 % |
Copper | 59 - 60.5 % |
Iron | 0.2 % |
Lead | 0.2 - 0.8 % |
Nickel | 0.3 % |
Tin | 0.2 % |
Metal
- EN 1652 CuNi30Mn1Fe R410 – Premium Copper-Nickel-Manganese Alloy
- EN 12164 CuZn38Pb1 (R490) Brass – Key Mechanical & Thermal Properties
- EN 12164 Grade CuZn38Pb2 R490 – Premium Wrought Copper Brass Specification
- EN 12164 Grade CuZn39Pb2 M – Lead-Enhanced Brass Alloy for Durable Applications
- EN 1652 Grade CuZn39Pb0.5 R540 – Unhardenable Wrought Alloy with Enhanced Machinability
- EN 12164 CuNi18Zn19Pb1 Grade H130 – High‑Strength, Corrosion‑Resistant Alloy
- EN 12164 Grade CuNi12Zn30Pb1 R650: High-Strength, Corrosion-Resistant Copper Alloy
- EN 12164 Grade CuNi18Zn19Pb1 R650 – High-Strength, Corrosion-Resistant Copper Alloy
- EN 12164 CuZn39Pb0.5 R360 Brass – Superior Strength & Machinability
- EN 12164 CuZn38Pb1 Grade – 410 MPa Copper–Zinc–Lead Alloy