EN 1652 CuNi30Mn1Fe R410 – Premium Copper-Nickel-Manganese Alloy

CuNi30Mn1Fe (CW354H) is comparable to CuNi30Mn1Fe, mat. no. 2.0882, acc. to DIN 17664 : 1983-12. To the comparable DIN-mark applies: The material shows favorable specific strength values also at endurance loading and increased temperatures. Thermal conductivity of pure copper is strongly reduced by Ni, the electrical resistance strongly increases according to the Ni-content. Fe-addition increases the corrosion resistance. CuNi30Mn1Fe is resistant to water and seawater, coolant and solvent, alkaline substances, alkaline saline solutions and non-oxidizing acids. warm forming: good cold forming: good machinability: moderately hard soldering: very good soft soldering: very good gas-shielded welding: very good burnishing: good Application: For seawater pipilines, tubes and plates for all types of tubular heat-exchanger (condenser, cooler, seawater evaporators, high pressure feeder water heater) on ships, in power plants, in petroleum processing an in chemical factories as well as in saltern plants. The material is established for condenser in ammoniac steam.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.9 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-253.0 °C

161 GPa

-195.0 °C

158 GPa

-100.0 °C

155 GPa

20.0 °C

150 GPa

50.0 °C

150 GPa

100.0 °C

149 GPa

150.0 °C

148 GPa

200.0 °C

146 GPa

250.0 °C

144 GPa

300.0 °C

142 GPa

350.0 °C

141 GPa

Elongation

20.0 °C

14 %

Elongation, transverse

20.0 °C

14 %

Hardness, Vickers

20.0 °C

140 [-]

Tensile strength

20.0 °C

410 MPa

Tensile strength, transverse

20.0 °C

410 MPa

Yield strength Rp0.2

20.0 °C

300 MPa

50.0 °C

300 MPa

100.0 °C

275 MPa

150.0 °C

265 MPa

200.0 °C

260 MPa

250.0 °C

255 MPa

300.0 °C

245 MPa

350.0 °C

240 MPa

Yield strength Rp0.2, transverse

20.0 °C

300 MPa

50.0 °C

300 MPa

100.0 °C

275 MPa

150.0 °C

255 - 265 MPa

200.0 °C

240 - 260 MPa

250.0 °C

255 MPa

300.0 °C

245 MPa

350.0 °C

240 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

300.0 °C

1.6E-5 1/K

Melting point

915 - 1240 °C

Typical for Wrought Copper Nickel Grade

Specific heat capacity

23.0 °C

375 - 398 J/(kg·K)

Typical for Wrought Copper Nickel Grade

Thermal conductivity

20.0 °C

29 W/(m·K)

Chemical properties

PropertyValue

Carbon

0.05 %

Cobalt

0.1 %

Iron

0.4 - 1 %

Lead

0.02 %

Manganese

0.5 - 1.5 %

Nickel

30 - 32 %

Phosphorus

0.02 %

Sulfur

0.05 %

Tin

0.05 %

Zinc

0.5 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 1652 CuCo1Ni1Be TH – High-Performance Copper Alloy for Industrial Applications
    2. EN 1652 Grade CuNi30Mn1Fe R350 – High-Strength, Corrosion-Resistant Copper Alloy
    3. EN 1652 Grade CuSn6 M – Premium Tin-Copper Alloy for Superior Corrosion Resistance
    4. EN 1652 Grade CuNi2Si M – High-Performance Copper Alloy for Superior Conductivity and Corrosion Resistance
    5. EN 1652 CuZn37 R410: High-Performance Copper Alloy for Cold Forming
    6. EN 1652 Grade CuZn15 (R410) – High-Strength, Corrosion-Resistant Copper Alloy
    7. EN 1652 Grade CuZn30 (CW505L) – Premium Unhardenable Wrought Copper Alloy for High-Strength Applications
    8. EN 1652 CuZn36 R410: Premium Unhardenable Copper Alloy for Superior Strength
    9. EN 1652 Grade CuNi2Be TH – High-Strength Low-Alloy Copper Alloy
    10. EN 1652 CuNi2Si TH: High-Performance Low-Alloy Copper Alloy