EN 12163 Grade CuZr R350 – High-Performance, Low Alloy Copper Alloy
CuZr, mat. No CW120C, is counted among hardenable, low alloyed copper alloys. To the comparable make CuZr, mat. No 2.1580, acc. to DIN 17666 : 1983-12 applies: The strength properties of CuZr are not as favorable as for CuCrZr but it very well meets high requirements to tempering strength and creep strength at preferably high electric conductivity.Temperature for removal of workhardening approximates 525°C. Processing properties: hot and cold forming: good machinability: moderately soft soldering: moderately hard soldering: moderately gas shielded welding: moderately burnishing: good Application: For commutator lamellae of high strains, rotor windings in high loaded electric motors, diode bases, resistance welding electrodes as well as for electronic calculators.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.9 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 135 GPa | |
Elongation | 20.0 °C | 12 % | |
Elongation A100 | 20.0 °C | 5 - 8 % | |
Elongation A11.3 | 20.0 °C | 10 % | |
Poisson's ratio | 23.0 °C | 0.34 [-] | Typical for Wrought Copper Pure / Low Alloyed Copper |
Shear modulus | 23.0 °C | 48 GPa | Typical for Wrought Copper Pure / Low Alloyed Copper |
Tensile strength | 20.0 °C | 350 MPa | |
Yield strength Rp0.2 | 20.0 °C | 260 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 300.0 °C | 1.7E-5 - 1.8E-5 1/K | |
Melting point | 965 - 1100 °C | Typical for Wrought Copper Pure / Low Alloyed Copper | |
Specific heat capacity | 23.0 °C | 377 - 420 J/(kg·K) | Typical for Wrought Copper Pure / Low Alloyed Copper |
Thermal conductivity | 20.0 °C | 167 - 330 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 2.60E+7 - 5.40E+7 S/m |
Specific Electrical conductivity | 86 % IACS |
Chemical properties
| Property | Value |
|---|---|
Zirconium | 0.1 - 0.2 % |
Metal
- EN 12163 CuZr TH Grade – High Strength Low‑Alloy Copper Alloy
- EN 12163 Grade CuZr H090 – High Strength, High Conductivity Copper Alloy
- EN 12163 Grade H120 CuZr Copper Alloy – High Strength, Excellent Conductivity
- EN 12163 Grade H075 CuZr Alloy – High Strength & Conductivity
- CuZn5 R350 – EN 12163 Grade Wrought Alloy for Electrical & Industrial Applications
- EN 12163 Grade CuNi10Fe1Mn R350 – High-Performance Corrosion-Resistant Alloy
- EN 12167 Grade CuZr R350: High-Performance Low-Carbon Copper Alloy for Superior Strength and Conductivity
- EN 12166 CuZr R350: Premium Grade Copper-Zirconium Alloy for High-Performance Applications
- EN 12163 Grade CuZr R280: High-Strength, High-Conductivity Copper Alloy
- EN 12163 Grade Cu-DLP R350 – High-Performance Deoxidized Copper