EN 12163 Grade CuNi10Fe1Mn R350 – High-Performance Corrosion-Resistant Alloy

CuNi10Fe1Mn (CW352H) is comparable to CuNi10Fe1Mn, mat. no. 2.0872, acc. to DIN 17664 : 1983-12. To the comparable DIN-mark applies: The material shows favorable specific strength values also at endurance loading and increased temperatures. Thermal conductivity of pure copper is strongly reduced by Ni, the electrical resistance strongly increases according to the Ni-content. Fe-addition increases the corrosion resistance. CuNi10Fe1Mn is resistant to seawater, alkaline saline solutions and non-oxidizing acids. warm forming: good cold forming: very good machinability: unfavorable hard soldering: very good soft soldering: very good gas-shielded welding: very good burnishing: good Application: For seawater pipilines, tubes and plates for all types of tubular heat-exchanger (condenser, cooler, seawater evaporators, high pressure feeder water heater) on ships, in power plants, seawater desalination plants, chemical and sugar factories.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.9 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-253.0 °C

153 GPa

-195.0 °C

148 GPa

-100.0 °C

142 GPa

20.0 °C

130 GPa

50.0 °C

129 GPa

100.0 °C

128 GPa

150.0 °C

127 GPa

200.0 °C

125 GPa

250.0 °C

122 GPa

300.0 °C

121 GPa

Elongation

20.0 °C

10 - 14 %

Elongation A10

20.0 °C

8 %

Elongation A100

20.0 °C

6 %

Elongation A11.3

20.0 °C

8 %

Elongation, transverse

20.0 °C

14 %

Hardness, Vickers

20.0 °C

120 [-]

Tensile strength

20.0 °C

350 MPa

Tensile strength, transverse

20.0 °C

350 MPa

Yield strength Rp0.2

20.0 °C

150 - 250 MPa

50.0 °C

250 MPa

100.0 °C

235 MPa

150.0 °C

225 MPa

200.0 °C

220 MPa

250.0 °C

210 MPa

300.0 °C

205 MPa

Yield strength Rp0.2, transverse

20.0 °C

250 MPa

50.0 °C

250 MPa

100.0 °C

235 MPa

150.0 °C

210 - 225 MPa

200.0 °C

205 - 220 MPa

250.0 °C

210 MPa

300.0 °C

205 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.4E-5 - 1.8E-5 1/K

Typical for Wrought Copper Nickel Grade

Melting point

915 - 1240 °C

Typical for Wrought Copper Nickel Grade

Specific heat capacity

20.0 °C

380 J/(kg·K)

Thermal conductivity

20.0 °C

50.2 W/(m·K)

Chemical properties

PropertyValue

Carbon

0.05 %

Cobalt

0.1 %

Iron

1 - 2 %

Lead

0.02 %

Manganese

0.5 - 1 %

Nickel

9 - 11 %

Phosphorus

0.02 %

Sulfur

0.05 %

Tin

0.03 %

Zinc

0.5 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 12163 CuZr TH Grade – High Strength Low‑Alloy Copper Alloy
    2. EN 12163 Grade CuBe2 M: High-Performance Hardenable Copper Alloy
    3. EN 12163 Grade CuZn10 M – High-Strength, Corrosion-Resistant Copper Alloy
    4. EN 12163 CuZn40 M: High-Performance Unhardenable Wrought Copper Alloy
    5. EN 12163: Grade CuZn33 M – High-Strength Unhardenable Wrought Copper Alloy
    6. EN 12163 Grade CuZn36 M – Premium Unhardenable Copper Alloy for Precision Deep Drawing
    7. CuZn5 R350 – EN 12163 Grade Wrought Alloy for Electrical & Industrial Applications
    8. EN 12163 Grade CuZr R350 – High-Performance, Low Alloy Copper Alloy
    9. EN 12163 Cu‑DHP R350: Premium Deoxidized Phosphoric Copper
    10. EN 12163 Grade Cu-DLP R350 – High-Performance Deoxidized Copper