EN 12163 Grade CuZn37 H105 – High-Performance Unhardenable Copper Alloy
CuZn37 (CW508L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn36. CuZn37 is the main alloy for cold forming. It shows favorable corrosion resistance to fresh water. Processing properties: warm forming: good cold forming: very good machinability: moderately hard soldering: good soft soldering: very good TIG-welding: moderately burnishing: very good CuZn37 is used for bulb bases, wire clamps for aerial lines, contact springs, metal and wooden screws, print roller and zip fastener. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.4 - 8.44 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 110 GPa | |
100.0 °C | 106 GPa | ||
200.0 °C | 102 GPa | ||
300.0 °C | 97 GPa | ||
400.0 °C | 89 GPa | ||
500.0 °C | 79 GPa | ||
Hardness, Brinell | 20.0 °C | 105 - 145 [-] | |
Hardness, Vickers | 20.0 °C | 110 - 140 [-] | |
Shear modulus | 23.0 °C | 40 GPa | Typical for Wrought Copper Brass |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 150.0 °C | 1.9E-5 1/K | |
300.0 °C | 2.1E-5 1/K | ||
650.0 °C | 2.3E-5 1/K | ||
800.0 °C | 2.4E-5 1/K | ||
Melting point | 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 20.0 °C | 377 J/(kg·K) | |
Thermal conductivity | -200.0 °C | 50 W/(m·K) | |
20.0 °C | 120 W/(m·K) | ||
200.0 °C | 142 W/(m·K) | ||
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 1.50E+7 S/m |
200.0 °C | 1.20E+7 S/m | |
Electrical resistivity | 20.0 °C | 6.6E-8 Ω·m |
200.0 °C | 8.3E-8 Ω·m | |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 0.05 % |
Copper | 62 - 64 % |
Iron | 0.1 % |
Lead | 0.1 % |
Nickel | 0.3 % |
Tin | 0.1 % |
Metal
- EN 12163 CuZr TH Grade – High Strength Low‑Alloy Copper Alloy
- EN 12163 Grade CuBe2 M: High-Performance Hardenable Copper Alloy
- EN 12163 Grade CuZn10 M – High-Strength, Corrosion-Resistant Copper Alloy
- EN 12163 CuZn40 M: High-Performance Unhardenable Wrought Copper Alloy
- EN 12163: Grade CuZn33 M – High-Strength Unhardenable Wrought Copper Alloy
- EN 12163 CuZn37 H140 – Premium Wrought Alloy for High Strength & Corrosion Resistance
- EN 12163 Grade CuZn39Sn1 (H105) – Premium Copper Alloy for High-Performance Applications
- EN 12163 Grade CuZn36 H105 – Premium Copper Alloy for High-Performance Applications
- EN 12163: CuZn37 H070 – High-Performance Copper Alloy for Cold Forming Applications
- EN 12163 Grade CuZn37 R310 – High-Strength Unhardenable Copper Alloy for Cold Forming