DIN 17200 Grade 28Cr4 Steel – Quenched & Tempered for Automotive & Machine Engineering Applications

Steel 28 Cr 4 is suitable for smaller parts of a little higher load in vehicle manufacturing, engine and machine engineering (e.g. transmission gears, drive shafts). Lowest application temp. -25 °C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.83 - 7.85 g/cm³

Mechanical

PropertyTemperatureValue

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

205 - 207 GPa

200.0 °C

195 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

175 - 184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

12 - 15 %

Poisson's ratio

20.0 °C

0.28 [-]

Reduction of area

20.0 °C

40 - 50 %

Shear modulus

20.0 °C

81 GPa

Tensile strength

20.0 °C

650 - 1000 MPa

Yield strength

20.0 °C

410 - 650 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.11E-5 - 1.21E-5 1/K

200.0 °C

1.21E-5 - 1.27E-5 1/K

300.0 °C

1.29E-5 - 1.32E-5 1/K

400.0 °C

1.35E-5 - 1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Max service temperature, long

-25 - 0 °C

Melting point

1382 - 1529 °C

Typical for Chromium Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

460 - 461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

45.1 - 46 W/(m·K)

100.0 °C

45.1 W/(m·K)

200.0 °C

44.1 W/(m·K)

300.0 °C

41.9 W/(m·K)

400.0 °C

39.4 W/(m·K)

500.0 °C

36.9 W/(m·K)

600.0 °C

34.4 W/(m·K)

Thermal diffusivity

20.0 °C

12.5 mm²/s

100.0 °C

11.6 mm²/s

200.0 °C

10.6 mm²/s

300.0 °C

9.5 mm²/s

400.0 °C

8.4 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.8 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.9E-7 - 2.31E-7 Ω·m

100.0 °C

2.84E-7 Ω·m

200.0 °C

3.58E-7 Ω·m

300.0 °C

4.48E-7 Ω·m

400.0 °C

5.52E-7 Ω·m

500.0 °C

6.71E-7 Ω·m

600.0 °C

8.06E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.24 - 0.31 %

Chromium

0.9 - 1.2 %

Manganese

0.6 - 0.9 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.03 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 17200 28CrS4 Quenched & Tempered Steel – High Strength for Automotive Gears & Shafts
    2. DIN 17200 Grade 28Mn6 Quenched & Tempered Steel – Key Properties & Applications
    3. DIN 17200 Grade 50CrMo4 Steel – Quenched & Tempered (QT) for High-Load Automotive & Machinery Applications
    4. DIN 17240 Grade C35 Quenched & Tempered Steel – High-Temperature Creep Resistance
    5. DIN 17240 Grade Ck 35 – Quenched & Tempered Steel for High-Temperature Bolt & Nut Applications
    6. DIN 17240 Grade Cq 35 Quenched & Tempered Steel – High-Temperature Creep-Resistant for Bolts & Nuts
    7. DIN 17200 Grade C35 Quenched & Tempered Steel – Ideal for Automotive & Machine Components
    8. DIN 17200 Grade C40 Quenched & Tempered Steel – Ideal for Heavy‑Duty Forged Components
    9. DIN 17200 Grade C45 Quenched & Tempered Steel – Optimal Performance for Automotive and Machinery Applications
    10. DIN 17200 Grade C22 Steel – Quenched & Tempered for Automotive & Machinery Applications