DIN 17200 Grade 28Mn6 Quenched & Tempered Steel – Key Properties & Applications

Steel 28 Mn 6 is suitable for lower strained parts in vehicle manufacturing, engine and machine engineering, weldable (e.g. cardan shafts, camshafts, gear wheels). Lowest application temp. -25 °C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.82 - 7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

205 - 207 GPa

200.0 °C

195 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

175 - 184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

13 - 16 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Manganese Steel

Reduction of area

20.0 °C

40 - 50 %

Shear modulus

20.0 °C

81 GPa

Tensile strength

20.0 °C

640 - 930 MPa

Yield strength

20.0 °C

440 - 590 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.11E-5 - 1.25E-5 1/K

200.0 °C

1.21E-5 - 1.3E-5 1/K

300.0 °C

1.29E-5 - 1.36E-5 1/K

400.0 °C

1.35E-5 - 1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature, long

-25 - 0 °C

Melting point

1382 - 1529 °C

Typical for Manganese Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 - 490 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

48 - 52 W/(m·K)

100.0 °C

48.9 W/(m·K)

200.0 °C

47.5 W/(m·K)

300.0 °C

44.7 W/(m·K)

400.0 °C

41.6 W/(m·K)

500.0 °C

38.6 W/(m·K)

600.0 °C

35.5 W/(m·K)

Thermal diffusivity

20.0 °C

13.3 mm²/s

100.0 °C

12.6 mm²/s

200.0 °C

11.5 mm²/s

300.0 °C

10.2 mm²/s

400.0 °C

8.9 mm²/s

500.0 °C

7.5 mm²/s

600.0 °C

6 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.2E-7 - 2.17E-7 Ω·m

100.0 °C

2.62E-7 Ω·m

200.0 °C

3.32E-7 Ω·m

300.0 °C

4.2E-7 Ω·m

400.0 °C

5.23E-7 Ω·m

500.0 °C

6.41E-7 Ω·m

600.0 °C

7.8E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.25 - 0.32 %

Manganese

1.3 - 1.65 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.03 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10083-2 Grade 28Mn6 Steel – Quenched & Tempered for Automotive & Machine Applications
    2. EN 10297‑1 Grade 28Mn6 Quenched & Tempered Steel (QT) – Key Mechanical Properties
    3. EN 10250-2 Grade 28Mn6 Quenched & Tempered Steel – Ideal for High-Performance Automotive and Machine Parts
    4. DIN 17200 28CrS4 Quenched & Tempered Steel – High Strength for Automotive Gears & Shafts
    5. DIN 17200 Grade 50CrMo4 Steel – Quenched & Tempered (QT) for High-Load Automotive & Machinery Applications
    6. DIN 17200 Grade 28Cr4 Steel – Quenched & Tempered for Automotive & Machine Engineering Applications
    7. DIN 17200 Grade C35 Quenched & Tempered Steel – Ideal for Automotive & Machine Components
    8. DIN 17200 Grade C40 Quenched & Tempered Steel – Ideal for Heavy‑Duty Forged Components
    9. DIN 17200 Grade C45 Quenched & Tempered Steel – Optimal Performance for Automotive and Machinery Applications
    10. DIN 17200 Grade C22 Steel – Quenched & Tempered for Automotive & Machinery Applications