EN 10083-1 Grade 30CrNiMo8: High-Performance Quenched & Tempered Steel for Heavy-Duty Applications

Steel 30CrNiMo8 is suitable for high loaded parts (also large forged parts) with high heat-treatment sections and favorable toughness properties in aircraft and heavy-vehicle construction, machine engineering (e.g. propeller shafts, connecting rods, transmission shafts). Furthermore for large forged parts (e.g. rotors, shafts, discs). Lowest working temperature -40 °C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.8 - 7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

210 - 212 GPa

100.0 °C

205 - 207 GPa

200.0 °C

195 - 199 GPa

300.0 °C

185 - 192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

9 - 12 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Nickel Chromium Molybdenum Steel

Reduction of area

20.0 °C

40 - 50 %

Shear modulus

20.0 °C

81 GPa

Tensile strength

20.0 °C

900 - 1450 MPa

Yield strength

20.0 °C

700 - 1050 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.11E-5 - 1.21E-5 1/K

200.0 °C

1.21E-5 - 1.27E-5 1/K

300.0 °C

1.29E-5 - 1.32E-5 1/K

400.0 °C

1.35E-5 - 1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Max service temperature, long

-40 - 0 °C

Melting point

1382 - 1529 °C

Typical for Nickel Chromium Molybdenum Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

460 - 461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

33.7 - 42 W/(m·K)

100.0 °C

36.2 - 50.3 W/(m·K)

200.0 °C

37.8 - 49 W/(m·K)

300.0 °C

37.2 - 47.8 W/(m·K)

400.0 °C

35.7 W/(m·K)

500.0 °C

34 W/(m·K)

600.0 °C

32 W/(m·K)

Thermal diffusivity

20.0 °C

9.4 mm²/s

100.0 °C

9.4 mm²/s

200.0 °C

9.2 mm²/s

300.0 °C

8.5 mm²/s

400.0 °C

7.6 mm²/s

500.0 °C

6.6 mm²/s

600.0 °C

5.4 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.9E-7 - 3.09E-7 Ω·m

100.0 °C

3.54E-7 Ω·m

200.0 °C

4.18E-7 Ω·m

300.0 °C

5.05E-7 Ω·m

400.0 °C

6.09E-7 Ω·m

500.0 °C

7.27E-7 Ω·m

600.0 °C

8.67E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.26 - 0.34 %

Chromium

1.8 - 2.2 %

Copper

0.4 %

Manganese

0.3 - 0.8 %

Molybdenum

0.3 - 0.5 %

Nickel

1.8 - 2.2 %

Phosphorus

0.03 - 0.04 %

Silicon

0.1 - 0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10083-1 Grade 51CrV4: Quenched & Tempered Steel (QT)
    2. EN 10263-4 Grade 30CrNiMo8 Steel – Quenched & Tempered (QT) for High‑Strength Screws
    3. EN 10297‑1 Grade 30CrNiMo8 (QT) – Comprehensive Mechanical & Physical Properties
    4. EN 10269 Grade 30CrNiMo8 – High‑Performance Quenched & Tempered Steel for Aircraft & Heavy Machinery
    5. EN 10083-1 Grade 25CrMo4 Quenched & Tempered Steel: High Strength & Ductility for Automotive & Engine Components
    6. EN 10083-1 Grade 34Cr4 Quenched & Tempered Steel (+QT) – High Performance for Automotive & Industrial Applications
    7. EN 10083-1 Grade 34CrMo4 Quenched & Tempered Steel: High Strength & Toughness for Automotive & Industrial Applications
    8. EN 10083‑1 Grade 34CrNiMo6 Steel – Quenched & Tempered (+QT) for High‑Load Applications
    9. EN 10083‑1 Grade C30E Quenched & Tempered Steel – Ideal for High‑Performance Vehicle & Machine Components
    10. EN 10083-1 Grade C30R Quenched & Tempered Steel – Ideal for Automotive & Engine Components