EN 10297‑1 Grade 30CrNiMo8 (QT) – Comprehensive Mechanical & Physical Properties

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.8 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

9 - 11 %

Elongation, transverse

20.0 °C

7 - 9 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Nickel Chromium Molybdenum Steel

Reduction of area

20.0 °C

40 - 50 %

Reduction of area, transverse

20.0 °C

40 - 50 %

Tensile strength

20.0 °C

1000 - 1450 MPa

Tensile strength, transverse

20.0 °C

1000 - 1450 MPa

Yield strength

20.0 °C

800 - 1050 MPa

Yield strength, transverse

20.0 °C

800 - 1050 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.21E-5 1/K

200.0 °C

1.27E-5 1/K

300.0 °C

1.32E-5 1/K

400.0 °C

1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Melting point

1382 - 1529 °C

Typical for Nickel Chromium Molybdenum Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

33.7 W/(m·K)

100.0 °C

36.2 W/(m·K)

200.0 °C

37.8 W/(m·K)

300.0 °C

37.2 W/(m·K)

400.0 °C

35.7 W/(m·K)

500.0 °C

34 W/(m·K)

600.0 °C

32 W/(m·K)

Thermal diffusivity

20.0 °C

9.4 mm²/s

100.0 °C

9.4 mm²/s

200.0 °C

9.2 mm²/s

300.0 °C

8.5 mm²/s

400.0 °C

7.6 mm²/s

500.0 °C

6.6 mm²/s

600.0 °C

5.4 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

3.09E-7 Ω·m

100.0 °C

3.54E-7 Ω·m

200.0 °C

4.18E-7 Ω·m

300.0 °C

5.05E-7 Ω·m

400.0 °C

6.09E-7 Ω·m

500.0 °C

7.27E-7 Ω·m

600.0 °C

8.67E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.26 - 0.34 %

Chromium

1.8 - 2.2 %

Manganese

0.3 - 0.6 %

Molybdenum

0.3 - 0.5 %

Nickel

1.8 - 2.2 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10263-4 Grade 30CrNiMo8 Steel – Quenched & Tempered (QT) for High‑Strength Screws
    2. EN 10297-1 Grade 25CrMo4 Quenched & Tempered Steel – Properties & Applications
    3. EN 10297‑1 Grade 30CrMoV9: Quenched & Tempered Steel (QT) – Key Mechanical & Physical Properties
    4. EN 10297-1 Grade 34CrMo4 Quenched & Tempered Steel – Properties & Performance
    5. EN 10297-1 Grade 34CrNiMo6 – Quenched & Tempered Steel: Detailed Mechanical Properties
    6. EN 10297-1 Grade 41Cr4 Quenched & Tempered Steel – Properties & Performance
    7. EN 10269 Grade 30CrNiMo8 – High‑Performance Quenched & Tempered Steel for Aircraft & Heavy Machinery
    8. EN 10297-1: Grade 36Mn5 Quenched & Tempered Steel – Specifications & Properties
    9. EN 10297-1 Grade Cm60 – Quenched & Tempered Steel: High Strength & Reliability
    10. EN 10297‑1 Grade 28Mn6 Quenched & Tempered Steel (QT) – Key Mechanical Properties