ASTM B211 Grade 4032 T86 Aluminum Alloy – Key Properties & Standards
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.7 g/cm³ | Typical for Wrought 4000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 69.0 - 71.0 GPa | Typical for Wrought 4000 Series Aluminium | |||
Elongation | 3.0 % | T86 | ASTM B211 | Bar, Rod, Wire | |
4.0 % | T86 | ASTM B211 | Bar, Rod, Wire | A50 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 4000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 4000 Series Aluminium | |||
Shear modulus | 26.0 GPa | Typical for Wrought 4000 Series Aluminium | |||
Tensile strength | 350.0 MPa | T86 | ASTM B211 | Bar, Rod, Wire |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.2e-05 - 2.2e-05 1/K | Typical for Wrought 4000 Series Aluminium |
Melting point | 520.0 - 630.0 °C | Typical for Wrought 4000 Series Aluminium |
Specific heat capacity | 864.0 J/(kg·K) | Typical for Wrought 4000 Series Aluminium |
Thermal conductivity | 138.0 - 155.0 W/(m·K) | Typical for Wrought 4000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 23000000.0 - 30000000.0 S/m | Typical for Wrought 4000 Series Aluminium |
Electrical resistivity | 3.8e-08 - 5e-08 Ω·m | Typical for Wrought 4000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.1 | T86 | ASTM B211 | Bar, Rod, Wire |
Copper | 0.5 - 1.3 % | T86 | ASTM B211 | Bar, Rod, Wire |
Iron | 1.0 | T86 | ASTM B211 | Bar, Rod, Wire |
Magnesium | 0.8 - 1.3 % | T86 | ASTM B211 | Bar, Rod, Wire |
Nickel | 0.5 - 1.3 % | T86 | ASTM B211 | Bar, Rod, Wire |
Silicon | 11.0 - 13.5 % | T86 | ASTM B211 | Bar, Rod, Wire |
Zinc | 0.25 | T86 | ASTM B211 | Bar, Rod, Wire |
Technological properties
| Property | ||
|---|---|---|
| Workability | Moderate Workability | |
Metal
- JIS H4140 Grade 4032 T6 Aluminium Alloy – Properties & Specifications
- ASTM B211 Grade 5056 H111 Aluminum Alloy – Comprehensive Properties Overview
- ASTM B211 Grade 5056 H12 – High Strength 5000 Series Aluminum Alloy
- ASTM B211 Grade 5056 H14 Aluminum Sheet: Comprehensive Specs & Performance
- ASTM B211 2111T8 Aluminum Alloy – Key Properties & Standards
- ASTM B211 Grade 5056-O Aluminium: Properties, Standards & Applications
- ASTM B211 Grade 5154 O: High-Performance 5000-Series Aluminum Alloy
- ASTM B211 Grade 6262 (T8) – High-Performance Aluminum Alloy for Machining & Corrosion Resistance
- ASTM B211 Grade 6262 T9: High-Strength, Corrosion-Resistant Aluminum Alloy
- ASTM B211 Grade 1100 O Aluminum Alloy – High Corrosion Resistance & Purity