15SMn13 Untreated Steel – ISO 683-4 Grade for Precision Turned Parts
The free-cutting steel 15SMn13, suitable for case-hardening, is used for production of turned parts.
Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 7.8 - 7.9 g/cm³ | Typical for Low Carbon Steel |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 200 - 215 GPa | Typical for Low Carbon Steel |
Hardness, Brinell | 20.0 °C | 125 - 181 [-] | |
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for Low Carbon Steel |
Shear modulus | 23.0 °C | 82 GPa | Typical for Low Carbon Steel |
Tensile strength | 20.0 °C | 420 - 610 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
Max service temperature | 500 °C | Typical for Carbon Steel | |
Melting point | 1480 - 1526 °C | Typical for Low Carbon Steel | |
Specific heat capacity | 23.0 °C | 465 J/(kg·K) | Typical for Low Carbon Steel |
Thermal conductivity | 23.0 °C | 25 - 93 W/(m·K) | Typical for Low Carbon Steel |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 23.0 °C | 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
Magnetic
| Property | Value | Comment |
|---|---|---|
Curie temperature | 770 °C | Typical for Low Carbon Steel |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.12 - 0.18 % |
Manganese | 0.9 - 1.3 % |
Phosphorus | 0.06 % |
Silicon | 0.4 % |
Sulfur | 0.08 - 0.18 % |
Metal
- ISO 683-4 Grade 35SPb20 Untreated – High‑Strength Free‑Cutting Steel for Automotive and Machinery Parts
- ISO 683-4 Grade 38SMn28 Untreated Steel – Ideal for High‑Strength Turned Parts
- ISO 683-4 Grade 38SMnPb28 Untreated: High-Machinability Quenchable Steel for Precision Turned Parts
- ISO 683-4 Grade 35S20 Untreated Steel – High-Performance Cutting and Quenching Properties
- ISO 683-4 Grade 10SPb20 Untreated: High-Performance Free-Cutting Steel
- ISO 683-4 Grade 11SMnPb30: Untreated, High-Machinability Free-Cutting Steel
- ISO 683-4 Grade 11SMnPb37 – Untreated, High‑Machinability Free‑Cutting Steel
- ISO 683-4 Grade 10S20 Untreated Steel – Superior Machinability & Ductility
- ISO 683-4 Grade 11SMn30 – Untreated Free-Cutting Steel
- ISO 683-4 Grade 11SMn37 Untreated – Free‑Cutting Steel Properties & Applications