ISO 683-4 Grade 11SMn37 Untreated – Free‑Cutting Steel Properties & Applications
Free-cutting steel 11SMn37 is not intended for heat-treatment and is preferred 11SMn30 for higher machinability and surface appearance demands due to its higher S-content. The Pb-alloyed steel 11SMnPb30 is replaced by 11SMn37 for lower machinability requirements. Increased crack sensitivity has to be considered. Therefore limited application for bulk parts in car industry as well as in apparatus and equipment engineering.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.83 - 7.85 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | -100.0 °C | 217 GPa | |
20.0 °C | 210 - 212 GPa | ||
100.0 °C | 207 GPa | ||
200.0 °C | 193 - 199 GPa | ||
300.0 °C | 185 - 192 GPa | ||
400.0 °C | 175 - 184 GPa | ||
500.0 °C | 175 GPa | ||
600.0 °C | 164 GPa | ||
Hardness, Brinell | 20.0 °C | 107 - 169 [-] | |
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for Low Carbon Steel |
Shear modulus | 20.0 °C | 81 GPa | |
Tensile strength | 20.0 °C | 360 - 570 MPa | |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | -100.0 °C | 1.08E-5 1/K | |
20.0 °C | 1.19E-5 1/K | ||
100.0 °C | 1.1E-5 - 1.25E-5 1/K | ||
200.0 °C | 1.18E-5 - 1.3E-5 1/K | ||
300.0 °C | 1.36E-5 1/K | ||
400.0 °C | 1.32E-5 - 1.41E-5 1/K | ||
500.0 °C | 1.45E-5 1/K | ||
600.0 °C | 1.49E-5 1/K | ||
Max service temperature | 500 °C | Typical for Carbon Steel | |
Melting point | 1480 - 1526 °C | Typical for Low Carbon Steel | |
Specific heat capacity | -100.0 °C | 423 J/(kg·K) | |
20.0 °C | 460 - 461 J/(kg·K) | ||
100.0 °C | 479 - 480 J/(kg·K) | ||
200.0 °C | 499 - 520 J/(kg·K) | ||
300.0 °C | 517 J/(kg·K) | ||
400.0 °C | 536 - 610 J/(kg·K) | ||
500.0 °C | 558 J/(kg·K) | ||
600.0 °C | 587 J/(kg·K) | ||
Thermal conductivity | -100.0 °C | 37.6 W/(m·K) | |
20.0 °C | 42.2 - 54.4 W/(m·K) | ||
100.0 °C | 43.2 W/(m·K) | ||
200.0 °C | 42.9 W/(m·K) | ||
300.0 °C | 41.2 W/(m·K) | ||
400.0 °C | 39.1 W/(m·K) | ||
500.0 °C | 36.6 W/(m·K) | ||
600.0 °C | 34.1 W/(m·K) | ||
Thermal diffusivity | -100.0 °C | 12.9 mm²/s | |
20.0 °C | 11.7 mm²/s | ||
100.0 °C | 11.2 mm²/s | ||
200.0 °C | 10.3 mm²/s | ||
300.0 °C | 9.4 mm²/s | ||
400.0 °C | 8.3 mm²/s | ||
500.0 °C | 7.1 mm²/s | ||
600.0 °C | 5.7 mm²/s | ||
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | -100.0 °C | 1.82E-7 Ω·m |
20.0 °C | 1.1E-7 - 2.47E-7 Ω·m | |
100.0 °C | 2.96E-7 Ω·m | |
200.0 °C | 3.68E-7 Ω·m | |
300.0 °C | 4.55E-7 Ω·m | |
400.0 °C | 5.56E-7 Ω·m | |
500.0 °C | 6.75E-7 Ω·m | |
600.0 °C | 8.13E-7 Ω·m | |
Magnetic
| Property | Value | Comment |
|---|---|---|
Curie temperature | 770 °C | Typical for Low Carbon Steel |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.14 % |
Manganese | 1 - 1.5 % |
Phosphorus | 0.11 % |
Silicon | 0.05 % |
Sulfur | 0.34 - 0.4 % |
Metal
- ISO 683-4 Grade 35SPb20 Untreated – High‑Strength Free‑Cutting Steel for Automotive and Machinery Parts
- ISO 683-4 Grade 38SMn28 Untreated Steel – Ideal for High‑Strength Turned Parts
- ISO 683-4 Grade 38SMnPb28 Untreated: High-Machinability Quenchable Steel for Precision Turned Parts
- ISO 683-4 Grade 35S20 Untreated Steel – High-Performance Cutting and Quenching Properties
- ISO 683-4 Grade 10SPb20 Untreated: High-Performance Free-Cutting Steel
- ISO 683-4 Grade 11SMnPb30: Untreated, High-Machinability Free-Cutting Steel
- ISO 683-4 Grade 11SMnPb37 – Untreated, High‑Machinability Free‑Cutting Steel
- 15SMn13 Untreated Steel – ISO 683-4 Grade for Precision Turned Parts
- ISO 683-4 Grade 10S20 Untreated Steel – Superior Machinability & Ductility
- ISO 683-4 Grade 11SMn30 – Untreated Free-Cutting Steel