EN 1653 CuAl10Ni5Fe4 R620 – Premium Copper‑Aluminum Alloy for High‑Temperature Boilers, Vessels & Storage Units
Copper aluminum plates, sheet and circles for boilers, pressure vessels and hot water storage units.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.6 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | -253.0 °C | 128 GPa | |
-195.0 °C | 123 GPa | ||
-100.0 °C | 122 GPa | ||
20.0 °C | 120 GPa | ||
50.0 °C | 120 GPa | ||
100.0 °C | 116 GPa | ||
150.0 °C | 115 GPa | ||
200.0 °C | 115 GPa | ||
250.0 °C | 110 GPa | ||
Elongation | 20.0 °C | 14 % | |
Elongation, transverse | 20.0 °C | 14 % | |
Hardness, Vickers | 20.0 °C | 180 [-] | |
Poisson's ratio | 23.0 °C | 0.33 [-] | Typical for Leaded Phosphor Bronze |
Shear modulus | 20.0 °C | 45 GPa | |
Tensile strength | 20.0 °C | 620 MPa | |
Tensile strength, transverse | 20.0 °C | 620 MPa | |
Yield strength Rp0.2 | 20.0 °C | 250 MPa | |
Yield strength Rp0.2, transverse | 20.0 °C | 270 MPa | |
50.0 °C | 270 MPa | ||
100.0 °C | 260 - 265 MPa | ||
150.0 °C | 250 - 260 MPa | ||
200.0 °C | 260 MPa | ||
250.0 °C | 250 MPa | ||
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.5E-5 - 1.9E-5 1/K | Typical for Leaded Phosphor Bronze |
Specific heat capacity | 20.0 °C | 420 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 50 - 57 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 4.00E+6 - 7.00E+6 S/m |
Specific Electrical conductivity | 10.3 % IACS |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 8.5 - 11 % |
Iron | 3 - 5 % |
Lead | 0.05 % |
Manganese | 1 % |
Nickel | 4 - 6 % |
Silicon | 0.2 % |
Tin | 0.1 % |
Zinc | 0.4 % |
Metal
- EN 12163 CuAl10Ni5Fe4 Wrought Alloy – High-Strength, Temperature-Resistant, Cold-Formable
- EN 1652 Grade CuNi12Zn24 R620: High Strength, Corrosion‑Resistant Copper Alloy
- EN 12164 Grade CuZn37Mn3Al2PbSi R620 – High-Performance Unhardenable Copper Alloy
- EN 12163 CuNi2Be R620: High-Strength Low-Alloy Copper Alloy for Advanced Applications
- EN 1653 CuAl10Ni5Fe4 R590 Copper Alloy Plates for Boilers and Pressure Vessels
- EN 12165 Grade CuAl10Ni5Fe4 H180 – High Strength, Temperature‑Resistant Copper Alloy
- EN 12163 Grade CuAl10Ni5Fe4 R680: High-Strength Wrought Alloy
- EN 1653 Grade CuZn39Pb0.5 R310 – High-Strength Leaded Brass for Boilers & Pressure Vessels
- EN 1653 Cu-DLP R200 Copper Plate – Premium Quality for Boilers & Pressure Vessels
- EN 1653 Cu-DHP R240 Copper Plates for Boilers and Pressure Vessels