AA Grade 1350 H12 – Detailed Standards & Properties
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.705 g/cm³ | H12 | AA Standards |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 69.0 GPa | H12 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 1000 Series Aluminium | ||
Shear modulus | 25.9 GPa | Typical for Wrought 1000 Series Aluminium | ||
Tensile strength | 95.0 MPa | H12 | AA Standards |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.36e-05 1/K | H12 | AA Standards | |
100 °C | 2.36e-05 1/K | H12 | AA Standards | ||
Melting point | 645.0 - 655.0 °C | H12 | AA Standards | ||
Specific heat capacity | 900.0 - 963.0 J/(kg·K) | Typical for Wrought 1000 Series Aluminium | |||
Thermal conductivity | 234 W/(m·K) | H12 | AA Standards |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 36000000.0 S/m | H12 | AA Standards |
Electrical resistivity | 2.78e-08 Ω·m | H12 | AA Standards |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 99.5 % | H12 | AA Standards |
Boron | 0.05 % | H12 | AA Standards |
Chromium | 0.01 % | H12 | AA Standards |
Copper | 0.05 % | H12 | AA Standards |
Gallium | 0.03 % | H12 | AA Standards |
Iron | 0.40 % | H12 | AA Standards |
Manganese | 0.01 % | H12 | AA Standards |
Silicon | 0.1 % | H12 | AA Standards |
Zinc | 0.05 % | H12 | AA Standards |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12, H111), poor (H14, H24, H16, H26, H18) | |
| Workability | general (condition): good (O, H12, H111, H14, H24), acceptable (H16, H26, H18) | |
Metal
- AA Standards Grade 1199 H12 Aluminium – Key Mechanical & Thermal Properties
- AA Standards Grade 5049 H12 – Detailed Aluminium Mechanical & Thermal Properties
- AA 1435 H12 Aluminium Standard – Key Mechanical Properties
- AA 5056 H12 Aluminium Alloy – Standards & Properties
- AA 1350 H14: Comprehensive Mechanical & Physical Properties Overview
- AA Standards Grade 1350 O: Comprehensive Properties & Mechanical Specifications
- AA 1350 Grade H16 – Comprehensive Mechanical & Thermal Properties
- AA 1350 Grade H19 Aluminium: Key Mechanical Properties & Standards
- Grade 3105 H12 Aluminium Alloy – Comprehensive AA Standards Overview
- AA 5005 Aluminum Alloy – H12 Standard Grade