AA 5005 Aluminum Alloy – H12 Standard Grade
Aluminum AA 5005 is a lean aluminum magnesium alloy with low density and excellent thermal conductivity. This medium strength non-heat-treatable alloy is known for its corrosion resistance in alkaline marine situations. Aluminum AA 5005 is readily machinable, and can be welded using TIG and MIG methods. It is important to note that anodizing is a critical part to how Aluminum AA 5005 is used.
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.7 g/cm³ | H12 | AA Standards, ASTM B209 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 69.0 GPa | H12 | AA Standards, ASTM B209 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Tensile strength | 125.0 - 165.0 MPa | H12 | AA Standards, ASTM B209 | |
140.0 MPa | H12 | AA Standards |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.38e-05 1/K | H12 | AA Standards, ASTM B209 | |
100 °C | 2.38e-05 1/K | H12 | AA Standards, ASTM B209 | ||
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 630.0 - 655.0 °C | H12 | AA Standards, ASTM B209 | ||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Thermal conductivity | 201 W/(m·K) | H12 | AA Standards, ASTM B209 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 30000000.0 S/m | H12 | AA Standards, ASTM B209 |
Electrical resistivity | 3.33e-08 Ω·m | H12 | AA Standards, ASTM B209 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.1 % | H12 | AA Standards, ASTM B209 |
Copper | 0.2 % | H12 | AA Standards, ASTM B209 |
Iron | 0.70 % | H12 | AA Standards, ASTM B209 |
Magnesium | 0.5 - 1.1 % | H12 | AA Standards, ASTM B209 |
Manganese | 0.2 % | H12 | AA Standards, ASTM B209 |
Silicon | 0.3 % | H12 | AA Standards, ASTM B209 |
Zinc | 0.25 % | H12 | AA Standards, ASTM B209 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12, H32), poor (H14, H34, H16, H18, H36, H38) | |
| Workability | general (condition): good (O, H12, H32), acceptable (H14, H34), poor(H16, H18, H36, H38) | |
Metal
- AA 1435 H12 Aluminium Standard – Key Mechanical Properties
- AA 5056 H12 Aluminium Alloy – Standards & Properties
- AA Grade 1350 H12 – Detailed Standards & Properties
- Grade 3105 H12 Aluminium Alloy – Comprehensive AA Standards Overview
- AA 5005 (H112) – Lightweight, Corrosion-Resistant Aluminum Alloy for Marine Applications
- AA Standards Grade 5005 H26 – High-Performance Aluminum Alloy for Marine Applications
- AA 5005 H18 Aluminum Alloy – Grade, Standards & Properties
- AA 5005 H16 – Durable, Corrosion‑Resistant Aluminum for Marine Applications
- AA 5005 H36 Aluminum Alloy: Properties, Uses, and Standards
- AA 5005 H38 – Lightweight, Corrosion-Resistant Aluminum Alloy for Marine and Industrial Use