AA Standards Grade 5005 H26 – High-Performance Aluminum Alloy for Marine Applications
Aluminum AA 5005 is a lean aluminum magnesium alloy with low density and excellent thermal conductivity. This medium strength non-heat-treatable alloy is known for its corrosion resistance in alkaline marine situations. Aluminum AA 5005 is readily machinable, and can be welded using TIG and MIG methods. It is important to note that anodizing is a critical part to how Aluminum AA 5005 is used.
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.7 g/cm³ | H26 | AA Standards, ASTM B209 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 69.0 GPa | H26 | AA Standards, ASTM B209 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Tensile strength | 160.0 - 200.0 MPa | H26 | AA Standards, ASTM B209 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.38e-05 1/K | H26 | AA Standards, ASTM B209 | |
100 °C | 2.38e-05 1/K | H26 | AA Standards, ASTM B209 | ||
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 630.0 - 655.0 °C | H26 | AA Standards, ASTM B209 | ||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Thermal conductivity | 201 W/(m·K) | H26 | AA Standards, ASTM B209 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 30000000.0 S/m | H26 | AA Standards, ASTM B209 |
Electrical resistivity | 3.33e-08 Ω·m | H26 | AA Standards, ASTM B209 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.1 % | H26 | AA Standards, ASTM B209 |
Copper | 0.2 % | H26 | AA Standards, ASTM B209 |
Iron | 0.70 % | H26 | AA Standards, ASTM B209 |
Magnesium | 0.5 - 1.1 % | H26 | AA Standards, ASTM B209 |
Manganese | 0.2 % | H26 | AA Standards, ASTM B209 |
Silicon | 0.3 % | H26 | AA Standards, ASTM B209 |
Zinc | 0.25 % | H26 | AA Standards, ASTM B209 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12, H32), poor (H14, H34, H16, H18, H36, H38) | |
| Workability | general (condition): good (O, H12, H32), acceptable (H14, H34), poor(H16, H18, H36, H38) | |
Metal
- AA Standard Grade 5010 H26 – Aluminium Properties & Specifications
- AA 1060 H26 Aluminium – ASTM B209 Standards and Properties
- AA Standards for Grade 3004 H26 Aluminium: Key Properties & Performance
- AA Standard Grade 3105 H26 Aluminium – Properties & Specifications
- AA Standards Grade 5252 H26 – Comprehensive Material Properties
- AA Standards Grade 5154 H26: Key Mechanical Properties & Specifications
- AA Standards Grade 5254 H26 Aluminium: Key Mechanical Properties & Specifications
- AA 5050 Grade H26 Aluminium – Mechanical Properties & Standards
- AA 5657 Alloy: Grade H26 – High Workability & Corrosion Resistance
- AA 1100 H26 Aluminum Alloy – Premium Corrosion-Resistant Grade