AA Standards Grade 5252 H26 – Comprehensive Material Properties
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.67 g/cm³ | H26 | AA Standards, ASTM B209 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 69.0 GPa | H26 | AA Standards, ASTM B209 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Tensile strength | 260.0 MPa | H26 | AA Standards, ASTM B209 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.38e-05 1/K | H26 | AA Standards, ASTM B209 | |
100 °C | 2.38e-05 1/K | H26 | AA Standards, ASTM B209 | ||
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 605.0 - 650.0 °C | H26 | AA Standards, ASTM B209 | ||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Thermal conductivity | 138 W/(m·K) | H26 | AA Standards, ASTM B209 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 20000000.0 S/m | H26 | AA Standards, ASTM B209 |
Electrical resistivity | 5e-08 Ω·m | H26 | AA Standards, ASTM B209 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Copper | 0.1 % | H26 | AA Standards, ASTM B209 |
Iron | 0.10 % | H26 | AA Standards, ASTM B209 |
Magnesium | 2.2 - 2.8 % | H26 | AA Standards, ASTM B209 |
Manganese | 0.1 % | H26 | AA Standards, ASTM B209 |
Silicon | 0.08 % | H26 | AA Standards, ASTM B209 |
Vanadium | 0.05 % | H26 | AA Standards, ASTM B209 |
Zinc | 0.05 % | H26 | AA Standards, ASTM B209 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: limited brazing | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (H24, H25), sufficient (H28) | |
| Workability | general (condition): acceptable (H24, H25), poor(H28) | |
Metal
- AA Standard Grade 5010 H26 – Aluminium Properties & Specifications
- AA 1060 H26 Aluminium – ASTM B209 Standards and Properties
- AA Standards for Grade 3004 H26 Aluminium: Key Properties & Performance
- AA Standard Grade 3105 H26 Aluminium – Properties & Specifications
- AA Standards Grade 5252 H25 Aluminium – Key Mechanical Properties & Specifications
- AA Standards Grade 5154 H26: Key Mechanical Properties & Specifications
- AA Standards Grade 5254 H26 Aluminium: Key Mechanical Properties & Specifications
- AA 5050 Grade H26 Aluminium – Mechanical Properties & Standards
- AA Standards Grade 5252 H24 – Key Mechanical Properties
- AA Standards Grade 5252 H28 – Comprehensive Mechanical & Physical Properties