C17500 Alloy 10 TH04 Wire – High Strength & Conductivity
Materion Performance Alloy 10 wire provides good strength with high electrical conductivity and good resistance to stress relaxation.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 8.83 g/cm³ |
Dimension
| Property | Value |
|---|---|
Diameter | 1.27 - 12.7 mm |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 138 GPa | |
Elongation | 23.0 °C | 10 % | min. |
Tensile strength | 23.0 °C | 750 - 970 MPa | |
Yield strength Rp0.2 | 23.0 °C | 650 - 870 MPa |
Thermal
| Property | Temperature | Value |
|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.76E-5 1/K |
Melting point | 1010 °C | |
Thermal conductivity | 23.0 °C | 200 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 23.0 °C | 2.9E-6 - 3.8E-6 Ω·m |
Specific Electrical conductivity | 45 - 60 % IACS |
Chemical properties
| Property | Value |
|---|---|
Beryllium | 0.4 - 0.7 % |
Cobalt | 2.4 - 2.7 % |
Copper | Balance |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Typical applications include coil springs and formed wire contacts. | |
Metal
- Alloy 10 (C17500) TF00 Wire – High Strength, Superior Conductivity
- M25 Copper Alloy Wire – Free-Milling, High-Performance, TH04 (C17300)
- Alloy 25 Wire TH04 – Premium High‑Strength Copper Alloy (C17200)
- High-Strength, High-Conductivity Alloy 3 (C17510) TH04 Wire
- Alloy 10 (C17500) TB00 Wire – High-Performance Strength & Conductivity
- Alloy 10 (C17500) TD04 Wire – High Strength, Excellent Conductivity & Stress Resistance
- High-Performance Alloy 10 (C17500) TH04 Tubing – Superior Conductivity & Strength
- Alloy 10X (C17500) TH04 Bar – High‑Temperature Copper Alloy for Superior Strength & Conductivity
- Alloy 10 (C17500) TH04 Plate – Exceptional Electrical & Thermal Conductivity with Balanced Strength
- High-Performance Alloy 10 (C17500) TH04 Rods and Bars – Superior Conductivity & Strength