EN 10277-2: Grade St 37-2 – Cold Drawn or Turned, Soft Annealed Steel

St 37-2 is used for moderate loaded parts, without inspection.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

25 - 26 %

Poisson's ratio

20.0 °C

0.28 [-]

Shear modulus

23.0 °C

82 GPa

Typical for Low Carbon Steel

Tensile strength

20.0 °C

440 - 470 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

56.9 W/(m·K)

100.0 °C

56.4 W/(m·K)

200.0 °C

53.5 W/(m·K)

300.0 °C

49.4 W/(m·K)

400.0 °C

45.2 W/(m·K)

500.0 °C

41.3 W/(m·K)

600.0 °C

37.6 W/(m·K)

Thermal diffusivity

20.0 °C

15.7 mm²/s

100.0 °C

14.5 mm²/s

200.0 °C

12.9 mm²/s

300.0 °C

11.2 mm²/s

400.0 °C

9.6 mm²/s

500.0 °C

7.9 mm²/s

600.0 °C

6.3 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.83E-7 Ω·m

100.0 °C

2.27E-7 Ω·m

200.0 °C

2.95E-7 Ω·m

300.0 °C

3.8E-7 Ω·m

400.0 °C

4.81E-7 Ω·m

500.0 °C

5.99E-7 Ω·m

600.0 °C

7.38E-7 Ω·m

Magnetic

PropertyValueComment

Curie temperature

770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Carbon

0.2 %

Phosphorus

0.05 %

Sulfur

0.05 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10277-2 Grade ZSt50-2: Cold‑Drawn or Turned, Soft‑Annealed Steel for High‑Performance Wear Parts
    2. EN 10277-2 Grade ZSt60-2: Cold‑Drawn, Soft‑Annealed Steel for High‑Strength, Wear‑Resistant Parts
    3. EN 10277-2 Grade ZSt70-2 – Cold Drawn/Turned, Soft‑Annealed High‑Carbon Steel
    4. EN 10277-2 Grade St 50-2: Cold-Drawn, Turned, Soft-Annealed Structural Steel for High-Strength Applications
    5. EN 10277-2 Grade St 60-2 – Cold Drawn, Turned & Soft Annealed Structural Steel
    6. EN 10277-2 Grade ZSt 37-2 – Cold-Drawn, Turned & Soft-Annealed Low-Carbon Steel
    7. EN 10277-2: Grade USt 37-2 – Cold Drawn, Turned, and Soft Annealed Steel
    8. EN 10277-2 Grade UZSt 37-2: Cold-Drawn, Turned & Soft-Annealed Steel for High-Performance Applications
    9. EN 10277-2 Grade RSt 37-2: Cold‑Drawn, Turned, Soft‑Annealed Steel for Low‑Temperature Applications
    10. EN 10277-2 Grade RZSt 37-2 – Cold‑Drawn, Turned & Soft‑Annealed Steel for Stress‑Dependent Welded Structures