ASTM B316 Grade 5052 H32 Aluminum – Superior Corrosion Resistance & Welding Performance
Aluminum ASTM 5052 is a non-heat treatable alloy with excellent finishing qualities. ASTM 5052 offers better corrosion resistance than most aluminum alloys, especially to salt water and marine atmospheres. This alloy can be readily welded using most common techniques and is in fact offers some of the best welding characteristics of all aluminum alloys.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.65 - 2.7 g/cm³ | Typical for Wrought 5000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 69.0 - 70.0 GPa | Typical for Wrought 5000 Series Aluminium | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | |||
Tensile strength | 215.0 - 255.0 MPa | H32 | ASTM B316 | Wire, Rod |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.2e-05 - 2.5e-05 1/K | Typical for Wrought 5000 Series Aluminium |
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Melting point | 560.0 - 655.0 °C | Typical for Wrought 5000 Series Aluminium |
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium |
Thermal conductivity | 112.0 - 205.0 W/(m·K) | Typical for Wrought 5000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 31000000.0 S/m | Typical for Wrought 5000 Series Aluminium |
Electrical resistivity | 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.15 - 0.35 % | H32 | ASTM B316 | Wire, Rod |
Copper | 0.1 | H32 | ASTM B316 | Wire, Rod |
Iron | 0.4 | H32 | ASTM B316 | Wire, Rod |
Magnesium | 2.2 - 2.8 % | H32 | ASTM B316 | Wire, Rod |
Manganese | 0.1 | H32 | ASTM B316 | Wire, Rod |
Silicon | 0.25 | H32 | ASTM B316 | Wire, Rod |
Zinc | 0.1 | H32 | ASTM B316 | Wire, Rod |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |
Metal
- ASTM B316 Grade 5056 H32 Aluminium Alloy – Properties & Specifications
- ASTM B316 Grade 7075 Aluminum Alloy – Superior Strength & Corrosion Resistance for Aerospace Applications
- ASTM B316 Grade 3003O Aluminum Alloy: High Corrosion Resistance & Easy Welding
- ASTM B316 Grade 2017 Aluminum Alloy – Strength, Ductility & Machinability
- ASTM B316 Grade 5005 H32 Aluminum Alloy – High Corrosion Resistance & Thermal Conductivity
- ASTM B316 Grade 5052‑O Aluminum Alloy: Superior Corrosion Resistance & Welding Performance
- ASTM B483 Grade 5052 H32 – Premium Marine-Grade Aluminum Alloy
- ASTM B211 Grade 5052 H32 Aluminum: High Corrosion Resistance & Superior Welding
- ASTM B210 5052 H32 Aluminum: Superior Corrosion Resistance & Welding Performance
- ASTM B234M Grade 5052 H32 Aluminum Alloy – Superior Corrosion Resistance & Welding