ASTM B234M Grade 5052 H32 Aluminum Alloy – Superior Corrosion Resistance & Welding
Aluminum ASTM 5052 is a non-heat treatable alloy with excellent finishing qualities. ASTM 5052 offers better corrosion resistance than most aluminum alloys, especially to salt water and marine atmospheres. This alloy can be readily welded using most common techniques and is in fact offers some of the best welding characteristics of all aluminum alloys.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.65 - 2.7 g/cm³ | Typical for Wrought 5000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 69.0 - 70.0 GPa | Typical for Wrought 5000 Series Aluminium | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | |||
Tensile strength | 215.0 MPa | H32 | ASTM B234M | Seamless Tube |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.2e-05 - 2.5e-05 1/K | Typical for Wrought 5000 Series Aluminium |
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Melting point | 560.0 - 655.0 °C | Typical for Wrought 5000 Series Aluminium |
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium |
Thermal conductivity | 112.0 - 205.0 W/(m·K) | Typical for Wrought 5000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 31000000.0 S/m | Typical for Wrought 5000 Series Aluminium |
Electrical resistivity | 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.15 - 0.35 % | H32 | ASTM B234M | Seamless Tube |
Copper | 0.1 | H32 | ASTM B234M | Seamless Tube |
Iron | 0.4 | H32 | ASTM B234M | Seamless Tube |
Magnesium | 2.2 - 2.8 % | H32 | ASTM B234M | Seamless Tube |
Manganese | 0.1 | H32 | ASTM B234M | Seamless Tube |
Silicon | 0.25 | H32 | ASTM B234M | Seamless Tube |
Zinc | 0.1 | H32 | ASTM B234M | Seamless Tube |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |
Metal
- ASTM B316 Grade 5052 H32 Aluminum – Superior Corrosion Resistance & Welding Performance
- ASTM B316 Grade 5052‑O Aluminum Alloy: Superior Corrosion Resistance & Welding Performance
- ASTM B483 Grade 5052 H32 – Premium Marine-Grade Aluminum Alloy
- ASTM B483 Grade 5052‑O Aluminum: Superior Corrosion Resistance & Welding Performance
- ASTM B211 Grade 5052 H32 Aluminum: High Corrosion Resistance & Superior Welding
- ASTM B241 Grade 5052-O Aluminum: Superior Corrosion Resistance & Weldability
- ASTM B210 5052 H32 Aluminum: Superior Corrosion Resistance & Welding Performance
- ASTM B210 Grade 5052-O: Premium Marine-Grade Aluminum Alloy
- ASTM B211 Grade 5052-O Aluminum Alloy: Superior Corrosion Resistance & Weldability
- AA 5052 H32 Aluminum Alloy – Superior Corrosion Resistance & Welding Performance