AA 2014 T3510 – High-Strength Aluminum Alloy with Superior Machinability
AA 2014 is an alloy with strength, machinability and welding capabilities, Aluminum Alloy AA 2014 is an excellent option. It is a precipitation hardening alloy that maintains strength after heat treatment.
Properties
General
| Property | Value | Condition |
|---|---|---|
Density | 3.0 g/cm³ | T3510 |
Mechanical
| Property | Value | Condition | Comment |
|---|---|---|---|
Elastic modulus | 73.0 GPa | T3510 | |
Elongation | 6.9 % | T3510 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |
Poisson's ratio | 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |
Shear modulus | 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | |
Tensile strength | 440.0 MPa | T3510 | |
Yield strength | 330.0 MPa | T3510 |
Thermal
| Property | Value | Condition |
|---|---|---|
Coefficient of thermal expansion | 2.3e-05 1/K | T3510 |
Melting point | 510.0 °C | T3510 |
Specific heat capacity | 870.0 J/(kg·K) | T3510 |
Thermal conductivity | 150.0 W/(m·K) | T3510 |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
| Property | Value | Condition |
|---|---|---|
Aluminium | 90.4 - 95.0 % | T3510 |
Chromium | 0.1 % | T3510 |
Copper | 3.9 - 5.0 % | T3510 |
Iron | 0.7 % | T3510 |
Magnesium | 0.2 - 0.8 % | T3510 |
Manganese | 0.4 - 1.2 % | T3510 |
Other | 0.15 % | T3510 |
Silicon | 0.5 - 1.2 % | T3510 |
Titanium | 0.15 % | T3510 |
Zinc | 0.25 % | T3510 |
Zirconium | 0.2 % | T3510 |
Technological properties
| Property | ||
|---|---|---|
| Workability | Moderate Workability | |
Metal
- JIS H4140 (2014) T4 Aluminum Alloy – Superior Strength & Machinability
- JIS H4140 Grade 2014 T6: High-Strength Precipitation-Hardening Aluminum Alloy
- JIS H4080 2014 O Grade Aluminum Alloy – High Strength & Weldability
- JIS H4080 Grade 2014 T4 Aluminum Alloy – Superior Strength & Machinability
- JIS H4080 2014 T6 Aluminum – High Strength & Machinability
- JIS H4040 Grade 2014 O: High-Performance 2000 Series Aluminium Alloy
- JIS H4040 Grade 2014 T4 Aluminum Alloy – High Strength & Superior Machinability
- JIS H4040 2014 T6 Aluminum Alloy – Superior Strength & Weldability
- AA 2014 T3511 Aluminum Alloy: Strength, Machinability & Weldability
- AA 2014 T351 Aluminum Alloy: Strength, Machinability, and Welding Performance