EN 573-3 Grade AW-6101 T4 Aluminum Alloy – High Conductivity & Strength
EN AW-6101 is an alloy that offers users a high electrical conductivity and good mechanical strength. Standard methods can be used to machine, weld, and form Aluminum EN AW-6101 and it is easily extruded. EN AW-6101 also offers good corrosion resistance, bendability, and formability. Unlike other aluminum alloys, EN AW-6101 can be both hot and cold worked.
Properties
General
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Density | 2.7 g/cm³ | T4 | EN 573-3, EN 1715-2 | Wire |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 69.0 GPa | T4 | EN 573-3, EN 1715-2 | Wire | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 6000 Series Aluminium | |||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | |||
Tensile strength | 150.0 MPa | T4 | EN 573-3, EN 1715-2 | Wire |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3399999999999996e-05 1/K | T4 | EN 573-3, EN 1715-2 | Wire | |
100 °C | 2.3399999999999996e-05 1/K | T4 | EN 573-3, EN 1715-2 | Wire | ||
Melting point | 620.0 - 655.0 °C | T4 | EN 573-3, EN 1715-2 | Wire | ||
Specific heat capacity | 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium | ||||
Thermal conductivity | 218.0 - 226.0 W/(m·K) | T4 | EN 573-3, EN 1715-2 | Wire |
Electrical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Electrical conductivity | 33000000.0 - 35000000.0 S/m | T4 | EN 573-3, EN 1715-2 | Wire |
Electrical resistivity | 2.86e-08 - 3.03e-08 Ω·m | T4 | EN 573-3, EN 1715-2 | Wire |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Boron | 0.06 % | T4 | EN 573-3, EN 1715-2 | Wire |
Chromium | 0.03 % | T4 | EN 573-3, EN 1715-2 | Wire |
Copper | 0.1 % | T4 | EN 573-3, EN 1715-2 | Wire |
Iron | 0.50 % | T4 | EN 573-3, EN 1715-2 | Wire |
Magnesium | 0.35 - 0.8 % | T4 | EN 573-3, EN 1715-2 | Wire |
Manganese | 0.03 % | T4 | EN 573-3, EN 1715-2 | Wire |
Silicon | 0.3 - 0.7 % | T4 | EN 573-3, EN 1715-2 | Wire |
Zinc | 0.1 % | T4 | EN 573-3, EN 1715-2 | Wire |
Technological properties
| Property | ||
|---|---|---|
| Workability | Excellent workability. | |
Metal
- EN 573-3 Grade 3.0505 F Aluminium Alloy: Properties & Standards
- EN 573-3 Grade 3.1305 F Aluminium Alloy – Key Mechanical Properties
- EN 573-3 Grade 3.1305 O Aluminium: Key Mechanical Properties & Standards
- EN 573-3 Grade 3.1305 O3 – Comprehensive Aluminium Alloy Specifications
- EN 573-3 Grade 3.3316 F – Key Properties & Standards for 5000 Series Aluminium
- EN 573-3 Grade 3.3549 F – Premium Aluminum Alloy with Expert R&D Support
- EN 573-3 AW‑1090 F Aluminium: Technical Specifications & Standards
- AW-5356 F Aluminum Alloy – EN 573‑3 Specification & Key Mechanical Properties
- EN 573-3 Grade AW-6101 T4 Aluminum Alloy – High Conductivity & Strength
- EN 573-3 Grade AW-6101 T1 Aluminum Alloy – Superior Conductivity & Strength