EN 10216-3: P355N Normalized/Normalized Formed Steel – High-Performance Pressure Vessel Material

Steel P355N is a weldable fine-grained construction steel (alloyed high-quality steel) for pressure vessel construction.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.83 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

22 %

Elongation, transverse

20.0 °C

20 %

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Medium Carbon Steel

Shear modulus

23.0 °C

75 - 80 GPa

Typical for Carbon Steel

Tensile strength

20.0 °C

450 - 650 MPa

Tensile strength, transverse

20.0 °C

450 - 650 MPa

Yield strength

20.0 °C

305 - 355 MPa

Yield strength, transverse

20.0 °C

305 - 355 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1380 - 1514 °C

Typical for Medium Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

-100.0 °C

37.6 W/(m·K)

20.0 °C

42.2 W/(m·K)

100.0 °C

43.2 W/(m·K)

200.0 °C

42.9 W/(m·K)

300.0 °C

41.2 W/(m·K)

400.0 °C

39.1 W/(m·K)

500.0 °C

36.6 W/(m·K)

600.0 °C

34.1 W/(m·K)

Thermal diffusivity

-100.0 °C

12.9 mm²/s

20.0 °C

11.7 mm²/s

100.0 °C

11.2 mm²/s

200.0 °C

10.3 mm²/s

300.0 °C

9.4 mm²/s

400.0 °C

8.3 mm²/s

500.0 °C

7.1 mm²/s

600.0 °C

5.7 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

-100.0 °C

1.82E-7 Ω·m

20.0 °C

2.47E-7 Ω·m

100.0 °C

2.96E-7 Ω·m

200.0 °C

3.68E-7 Ω·m

300.0 °C

4.55E-7 Ω·m

400.0 °C

5.56E-7 Ω·m

500.0 °C

6.75E-7 Ω·m

600.0 °C

8.13E-7 Ω·m

Chemical properties

PropertyValue

Aluminium

0.02 %

Carbon

0.2 %

Chromium

0.3 %

Copper

0.3 %

Manganese

0.9 - 1.7 %

Molybdenum

0.08 %

Nickel

0.5 %

Niobium

0.05 %

Nitrogen

0.02 %

Phosphorus

0.03 %

Silicon

0.5 %

Sulfur

0.02 %

Titanium

0.04 %

Vanadium

0.1 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10216-3 Grade P460NL1 – Normalized & Normalized Formed Cryogenic Weldable Steel
    2. EN 10216-3 P460NL2 Steel – Normalized/Normalized Formed (+N) for Cryogenic Applications
    3. EN 10216-3 Grade P460NH – High‑Temperature Weldable Steel (Normalized/Normalized Formed +N)
    4. EN 10217-3 Grade P355N: Normalized & Normalized Formed Steel for Pressure Vessels & Pipelines
    5. EN 10216-3 Grade P355NL1: Normalized or Normalized Formed Steel for Cryogenic Applications
    6. EN 10216-3 Grade P355NL2 – Normalized / Normalized-Formed Steel (+N)
    7. EN 10216‑3 P460N Steel – Normalized/Normalized‑Formed, Ideal for Pressure Vessels
    8. EN 10216-3 Grade P275NL1 – High-Performance Cryogenic Weldable Steel (Normalized/Norm Formed)
    9. EN 10216‑3: Grade P275NL2 – Normalized / Normalized‑Formed Steel for Cryogenic Welding
    10. EN 10216-3 Grade P355NH: Normalized/Normalized Formed (+N) High-Temperature Weldable Steel