EN 12166 CuZn15 O60 – Premium Copper Alloy for Electrical & Jewelry Applications

CuZn15 (CW502L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for CuZn10. Corrosion resistance is similar to pure copper. Processing properties: warm forming: moderately cold forming: good machinability: moderately hard and soft soldering: very good TIG-welding: good burnishing: very good CuZn15 is used in electrical engineering, for metal goods as well as in jewelry industry, for metall hoses, pressure measuring instruments, signs, casings and suspension bodies. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Properties

General

PropertyTemperatureValue

Density

20.0 °C

8.75 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

20.0 °C

122 GPa

Elongation

20.0 °C

42 - 45 %

Elongation A10

20.0 °C

40 %

Elongation A100

20.0 °C

25 - 30 %

Hardness, Brinell

20.0 °C

45 - 75 [-]

Hardness, Vickers

20.0 °C

50 - 125 [-]

Poisson's ratio

20.0 °C

0.34 [-]

Shear modulus

23.0 °C

40 GPa

Typical for Wrought Copper Brass

Tensile strength

20.0 °C

260 - 410 MPa

Yield strength Rp0.2

20.0 °C

120 - 150 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.7E-5 - 2.1E-5 1/K

Typical for Wrought Copper Brass

Melting point

875 - 1075 °C

Typical for Wrought Copper Brass

Specific heat capacity

20.0 °C

380 J/(kg·K)

Thermal conductivity

20.0 °C

159 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

2.10E+7 S/m

Specific Electrical conductivity

36 % IACS

Chemical properties

PropertyValue

Aluminium

0.02 %

Copper

84 - 86 %

Iron

0.05 %

Lead

0.05 %

Nickel

0.3 %

Tin

0.1 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 12166 Copper Brass Grade CuZn15 R310 – Specifications & Properties
    2. EN 12166 Grade CuNi10Zn27 O60: High-Performance Copper-Nickel-Zinc Wire
    3. EN 12166 Grade CuZn15 H135 – Premium Copper Alloy Wire for Industrial Applications
    4. EN 12166 Grade CuZn15 H155 – High‑Quality Copper Alloy Wire for Industrial Applications
    5. EN 12166 Grade CuZn15 H060: High-Quality Copper Alloy Wire
    6. EN 12166 Grade CuZn15 R480 – Premium Unhardenable Copper Alloy for Electrical and Jewelry Applications
    7. EN 12166 Grade CuSn5 O60 – High‑Conductivity Copper Tin Alloy for Precision Tubes and Connectors
    8. EN 12166 Grade CuZn39Pb3 – Leaded Brass with Enhanced Machinability
    9. EN 12166 CuZn15 (R300) Wrought Copper Alloy – Superior Electrical Conductivity & Corrosion Resistance
    10. EN 12166 Grade CuNi12Zn24 O60 – High-Strength, Corrosion-Resistant Copper-Nickel-Zinc Alloy