ASTM B241 Grade 7075 Alloy – High-Strength, Corrosion-Resistant, Ideal for Aerospace Applications
ASTM 7075 is a high-strength alloy that offers good stress-corrosion cracking resistance. Known as a mainstay in the aerospace industry since it was introduced, Aluminum 7075 brings moderate toughness as well as an excellent strength-to-weight ratio. It is also important to note that at sub-zero temperatures Aluminum 7075 increases in strength.
Additional services: Cuttings, Parts from drawingsSTEEL SCOUT
DISTRIBUTOR
Information and services
Quantity: 1 PCSProperties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.7 - 2.85 g/cm³ | Typical for Wrought 7000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 69.0 - 72.0 GPa | Typical for Wrought 7000 Series Aluminium | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 7000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 7000 Series Aluminium | |||
Shear modulus | 26.4 - 27.1 GPa | Typical for Wrought 7000 Series Aluminium | |||
Tensile strength | 470.0 MPa | T73, T73510, T73511; Area through 13000 mm2 | ASTM B241 | Tube |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.1e-05 - 2.4e-05 1/K | Typical for Wrought 7000 Series Aluminium |
Melting point | 465.0 - 655.0 °C | Typical for Wrought 7000 Series Aluminium |
Specific heat capacity | 795.0 - 1050.0 J/(kg·K) | Typical for Wrought 7000 Series Aluminium |
Thermal conductivity | 121.0 - 170.0 W/(m·K) | Typical for Wrought 7000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 34000000.0 S/m | Typical for Wrought 7000 Series Aluminium |
Electrical resistivity | 2.9e-08 - 5.6e-08 Ω·m | Typical for Wrought 7000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.18 - 0.28 % | T73, T73510, T73511; Area through 13000 mm2 | ASTM B241 | Tube |
Copper | 1.2 - 2.0 % | T73, T73510, T73511; Area through 13000 mm2 | ASTM B241 | Tube |
Iron | 0.5 | T73, T73510, T73511; Area through 13000 mm2 | ASTM B241 | Tube |
Magnesium | 2.1 - 2.9 % | T73, T73510, T73511; Area through 13000 mm2 | ASTM B241 | Tube |
Manganese | 0.3 | T73, T73510, T73511; Area through 13000 mm2 | ASTM B241 | Tube |
Silicon | 0.4 | T73, T73510, T73511; Area through 13000 mm2 | ASTM B241 | Tube |
Titanium | 0.2 | T73, T73510, T73511; Area through 13000 mm2 | ASTM B241 | Tube |
Zinc | 5.1 - 6.1 % | T73, T73510, T73511; Area through 13000 mm2 | ASTM B241 | Tube |
Technological properties
| Property | ||
|---|---|---|
| Brazing | Excellent | |
Metal
- ASTM B241 Grade 5454 H111 – 20,000 mm² Tube Area (Aluminium)
- ASTM B241 Grade 5456 H111 Aluminium Tube – 20,000 mm² Cross-Section
- ASTM B241 Grade 5456 Aluminium Tube – 20,000 mm² Area Specification
- ASTM B241 Grade 5454 O – 20,000 mm² Tube Specification
- High-Strength ASTM B210 Grade 7075 T73 Aluminum Alloy – Aerospace-Grade Performance
- ASTM B241 Grade 7075 O Aluminum: High-Strength Alloy for Aerospace
- ASTM B316 Grade 7075 T73: Premium Aerospace-Grade Aluminum Alloy
- ASTM B241 Grade 5086 H112 Aluminum: Superior Strength & Corrosion Resistance, Up to 20,000 mm² Area
- ASTM B241 Grade 5086 O Aluminum – Strong, Corrosion‑Resistant Alloy up to 20,000 mm²
- ASTM B241 Grade 5086 H111 Aluminum – High Strength & Corrosion Resistance (≤ 20,000 mm²)