Quend 1100: Premium 1100 MPa High-Strength Structural Steel

Quend 1100 is recommended for the applications where high load-bearing capacity is required:

The steel is fine grain treated.

Quend 1100 is very well suited for cold forming operations.

*R = Recommended punch radius (mm), t = Plate thickness (mm) , W – Die opening width (mm) (bending angle ≤ 90°)

Due to the homogeneous properties and narrow thickness tolerances of Quend 1100, variations in springback are kept at a low level. Grinding of flame cut or a sheared edge in the bending area is recommended to further prevent cracking during bending.

Quend 1100 is delivered as quenched and tempered. Our Quend plates are supplied as standard in the shotblasted and painted condition. In order to maintain a good weldability and laser cutting performance, a low zinc silicate primer is applied. Plates can also be delivered unpainted.

The mechanical properties of Quend 1100 has been obtained by quenching and tempering. For not losing the guaranteed properties of Quend 1100, the plate should not be used in applications requiring hot working and service temperatures above 200 °C.

Quend 1100 provides a very good machinability and can be drilled, counter sinked and milled in the same way as any other 1100MPa Q&T steel.

Quend 1100 is delivered as quenched and tempered. Our Quend plates are supplied as standard in the shotblasted and painted condition. In order to maintain a good weldability and laser cutting performance, a low zinc silicate primer is applied. Plates can also be delivered unpainted.

Ultra sonic testing (UT), is applied to secure the plate from discontinuities like inclusions, cracks and porosity. In thickness from 8 mm and up, all plates are UT tested and controlled against class S2, E2, according to EN 10160.

Quend 1100 may be cut either by oxygen fuel, plasma and laser cutting without any restrictions. Subsequent to cutting, let the cut parts slowly cool down to room temperature. Do never accelerate the cooling of the parts. A slow cooling rate will reduce the risk of cut edge cracking.

Welding of Quend 1100 can be performed using any of the conventional welding methods available both as manual or automatic.

In the thickness range up to 10 mm, preheating prior to welding is normally not needed, if a heat input of 1,7 kJ/mm is used. Welding of Quend 1100 is recommended to be performed at ambient temperature not lower than +5 °C. Subsequent to welding, let the welded parts slowly cool down to room temperature. Do never accelerate the cooling process of the weld.

It is always recommended to use low hydrogen electrodes when welding Quend 1100.