JIS H4000 Grade 1100 O Aluminum Alloy – 99% Pure, High Corrosion Resistance
JIS 1100 is a soft, non-heat-treatable and low strength alloy that offers strong corrosion resistance. Composed of 99% aluminum and 0.12% copper, JIS 1100 is purest grade of aluminum alloy available commercially.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.7 g/cm³ | Typical for Wrought 1000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 68.0 - 70.0 GPa | Typical for Wrought 1000 Series Aluminium | |||
Elongation | 25.0 % | O | JIS H4000 | Plate, Sheet | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 1000 Series Aluminium | |||
Shear modulus | 25.9 GPa | Typical for Wrought 1000 Series Aluminium | |||
Tensile strength | 78.0 MPa | O | JIS H4000 | Plate, Sheet | |
Yield strength | 29.0 MPa | O | JIS H4000 | Plate, Sheet |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.2e-05 - 2.5e-05 1/K | Typical for Wrought 1000 Series Aluminium |
Melting point | 645.0 - 660.0 °C | Typical for Wrought 1000 Series Aluminium |
Specific heat capacity | 900.0 - 963.0 J/(kg·K) | Typical for Wrought 1000 Series Aluminium |
Thermal conductivity | 167.0 - 244.0 W/(m·K) | Typical for Wrought 1000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 33000000.0 - 38000000.0 S/m | Typical for Wrought 1000 Series Aluminium |
Electrical resistivity | 2.7e-08 - 3e-08 Ω·m | Typical for Wrought 1000 Series Aluminium |
Technological properties
| Property | ||
|---|---|---|
| Brazing | Excellent | |
| Processing history | O | |
| Workability | Excellent workability. | |
Metal
- JIS H4000 Grade 7N01 T4 – High-Strength 7000 Series Aluminium Alloy
- JIS H4000 Grade 7N01 T6: Premium 7000 Series Aluminum Alloy
- JIS Z3232 Grade 1100 O Aluminum: Superior Corrosion Resistance & High Purity
- JIS H4140 Grade 1100 Aluminum Alloy – Exceptional Corrosion Resistance
- JIS H4080 Grade 1100 Aluminum Tube – High Corrosion Resistance & Superior Purity
- 2024‑T4 Aluminum (JIS H4000): High Strength & Excellent Machinability for Aerospace Applications
- JIS H4000 Grade 2024 T3 Aluminum Alloy – High Strength, Aircraft‑Grade Machinability
- JIS H4000 Grade 1100 H18 – Premium Corrosion‑Resistant Aluminum Alloy
- JIS H4000 1100 Hot-Rolled Aluminum – High Corrosion Resistance & Purest Alloy
- JIS H4090 Grade 1100 O – Premium 99% Aluminum Alloy with Superior Corrosion Resistance