JIS H4000 Grade 7N01 T6: Premium 7000 Series Aluminum Alloy

Properties

General

Property	Value	Comment
Density	2.7 - 2.85 g/cm³	Typical for Wrought 7000 Series Aluminium

Mechanical

Property	Value	Condition	Related Standards	Comment
Elastic modulus	69.0 - 72.0 GPa			Typical for Wrought 7000 Series Aluminium
Elongation	10.0 %	T6	JIS H4000
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 7000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 7000 Series Aluminium
Shear modulus	26.4 - 27.1 GPa			Typical for Wrought 7000 Series Aluminium
Tensile strength	333.0 MPa	T6	JIS H4000
Yield strength	275.0 MPa	T6	JIS H4000

Thermal

Property	Value	Comment
Coefficient of thermal expansion	2.1e-05 - 2.4e-05 1/K	Typical for Wrought 7000 Series Aluminium
Melting point	465.0 - 655.0 °C	Typical for Wrought 7000 Series Aluminium
Specific heat capacity	795.0 - 1050.0 J/(kg·K)	Typical for Wrought 7000 Series Aluminium
Thermal conductivity	121.0 - 170.0 W/(m·K)	Typical for Wrought 7000 Series Aluminium

Electrical

Property	Value	Comment
Electrical conductivity	18000000.0 - 34000000.0 S/m	Typical for Wrought 7000 Series Aluminium
Electrical resistivity	2.9e-08 - 5.6e-08 Ω·m	Typical for Wrought 7000 Series Aluminium

Technological properties

Property

Brazing

Excellent

Processing history

T6