JIS H4000 Grade 2024 T3 Aluminum Alloy – High Strength, Aircraft‑Grade Machinability
Aluminum JIS 2024, known for its use in aircraft industry, is an alloy that offers excellent strength. When in the annealed condition it is readily formed and has good machinability. Though it has a relatively low level of corrosion resistance, it can be machined to a high finish.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.75 - 2.84 g/cm³ | Typical for Wrought 2000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 70.0 - 73.0 GPa | Typical for Wrought 2000 Series Aluminium | ||
Elongation | 15.0 % | T3 | JIS H4000 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||
Shear modulus | 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | ||
Tensile strength | 441.0 MPa | T3 | JIS H4000 | |
Yield strength | 294.0 MPa | T3 | JIS H4000 |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium |
Melting point | 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium |
Specific heat capacity | 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium |
Thermal conductivity | 112.0 - 251.0 W/(m·K) | Typical for Wrought 2000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Technological properties
| Property | ||
|---|---|---|
| Processing history | T3 | |
| Workability | Moderate Workability | |
Metal
- Premium Hot-Rolled JIS H4000 3203 Aluminium – Superior Strength & Reliability
- JIS H4000 Grade 7N01 T4 – High-Strength 7000 Series Aluminium Alloy
- JIS H4000 Grade 7N01 T6: Premium 7000 Series Aluminum Alloy
- JIS H4100 2024-O Aluminum Alloy – High Strength, Aircraft‑Grade Performance
- 2024 T4 Aluminum (JIS H4100) – High Strength, Aerospace‑Grade, Machinable Alloy
- 2024-T4 Aluminum (JIS H4080) – Aircraft-Grade, High-Strength Alloy
- 2024‑T4 Aluminum (JIS H4000): High Strength & Excellent Machinability for Aerospace Applications
- JIS H4040 2024 T4 Aluminum Alloy – High Strength for Aerospace Applications
- JIS H4000 Grade 2024 O – Premium 2024 Aluminium Alloy for Aerospace Applications
- JIS H4000 Grade 1100 O Aluminum Alloy – 99% Pure, High Corrosion Resistance