JIS H4000 Grade 3003 O Aluminum Alloy – Superior Corrosion Resistance & Weldability
Aluminum JIS 3003 is a popular alloy that offers customers very good atmospheric corrosion resistance and moderate strength. Aluminum 3003 offers good machinability for aluminum alloys, though it is not heat treatable. Unlike other aluminum alloys, JIS 3003 is weldable by conventional welding methods. It also takes cold and hot working well and has generally better mechanical properties when compared to 1000 series aluminum alloys.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.72 - 2.73 g/cm³ | Typical for Wrought 3000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 69.5 - 70.0 GPa | Typical for Wrought 3000 Series Aluminium | |||
Elongation | 23.0 % | O | JIS H4000 | Plate, Sheet | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 3000 Series Aluminium | |||
Shear modulus | 25.0 - 26.0 GPa | Typical for Wrought 3000 Series Aluminium | |||
Tensile strength | 98.0 MPa | O | JIS H4000 | Plate, Sheet | |
Yield strength | 39.0 MPa | O | JIS H4000 | Plate, Sheet |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.2e-05 - 2.4e-05 1/K | Typical for Wrought 3000 Series Aluminium |
Melting point | 629.0 - 654.0 °C | Typical for Wrought 3000 Series Aluminium |
Specific heat capacity | 893.0 - 920.0 J/(kg·K) | Typical for Wrought 3000 Series Aluminium |
Thermal conductivity | 154.0 - 193.0 W/(m·K) | Typical for Wrought 3000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 23000000.0 - 29000000.0 S/m | Typical for Wrought 3000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 4.2e-08 Ω·m | Typical for Wrought 3000 Series Aluminium |
Technological properties
| Property | ||
|---|---|---|
| Processing history | O | |
| Workability | Good workability. | |
Metal
- JIS H4100 3003 Aluminum Alloy – Superior Corrosion Resistance & Versatile Performance
- JIS H4040 Grade 3003 Aluminum Alloy – Superior Corrosion Resistance & Weldability
- JIS H4080 3003 Aluminum Alloy – Superior Corrosion Resistance & Weldability
- JIS 3003 Hot-Rolled Aluminum – Durable, Corrosion-Resistant, and Easy to Machine
- JIS 3003 O Aluminum Alloy – Superior Corrosion Resistance & Weldability
- JIS 3003 Aluminum Alloy – Superior Corrosion Resistance & Machinability
- JIS H4000 7075-O Aluminum Alloy – High Strength & Corrosion Resistance
- JIS H4000 Grade 7075 T6 Aluminum Alloy – High Strength & Corrosion Resistance
- JIS 2017 H4000 Grade Aluminum Alloy – High Strength, Excellent Machinability & Corrosion Resistance
- JIS H4000 Grade 2017 T4 Aluminum: Superior Strength & Machinability