JIS H4000 7075-O Aluminum Alloy – High Strength & Corrosion Resistance
JIS 7075 is a high-strength alloy that offers good stress-corrosion cracking resistance. Known as a mainstay in the aerospace industry since it was introduced, Aluminum 7075 brings moderate toughness as well as an excellent strength-to-weight ratio. It is also important to note that at sub-zero temperatures Aluminum 7075 increases in strength.
Additional services: Cuttings, Parts from drawingsSTEEL SCOUT
DISTRIBUTOR
Information and services
Quantity: 1 PCSProperties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.7 - 2.85 g/cm³ | Typical for Wrought 7000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 69.0 - 72.0 GPa | Typical for Wrought 7000 Series Aluminium | |||
Elongation | 10.0 % | O | JIS H4000 | Plate, Sheet, Strip | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 7000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 7000 Series Aluminium | |||
Shear modulus | 26.4 - 27.1 GPa | Typical for Wrought 7000 Series Aluminium | |||
Tensile strength | 275.0 MPa | O | JIS H4000 | Plate, Sheet, Strip | |
Yield strength | 147.0 MPa | O | JIS H4000 | Plate, Sheet, Strip |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.1e-05 - 2.4e-05 1/K | Typical for Wrought 7000 Series Aluminium |
Melting point | 465.0 - 655.0 °C | Typical for Wrought 7000 Series Aluminium |
Specific heat capacity | 795.0 - 1050.0 J/(kg·K) | Typical for Wrought 7000 Series Aluminium |
Thermal conductivity | 121.0 - 170.0 W/(m·K) | Typical for Wrought 7000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 34000000.0 S/m | Typical for Wrought 7000 Series Aluminium |
Electrical resistivity | 2.9e-08 - 5.6e-08 Ω·m | Typical for Wrought 7000 Series Aluminium |
Technological properties
| Property | ||
|---|---|---|
| Brazing | Excellent | |
| Processing history | O | |
Metal
- JIS H4100 Grade 7075 O Aluminum: High-Strength, Aerospace-Grade Alloy
- JIS H4100 Grade 7075 T6 Aluminum – High-Strength, Corrosion-Resistant Alloy
- JIS H4140 Grade 7075 T6 – High‑Strength Aerospace‑Grade Aluminum Alloy
- JIS H4040 Grade 7075 O – Premium Aerospace-Grade Aluminum Alloy
- JIS H4040 Grade 7075 T6 – High‑Strength Aluminum Alloy for Aerospace Applications
- JIS H4080 Grade 7075 O – High-Strength Aerospace Aluminum Alloy
- JIS H4080 Grade 7075 T6 Aluminum Alloy – High-Strength Aerospace Grade
- JIS H4000 Grade 3003 O Aluminum Alloy – Superior Corrosion Resistance & Weldability
- JIS H4000 Grade 7075 T6 Aluminum Alloy – High Strength & Corrosion Resistance
- JIS 2017 H4000 Grade Aluminum Alloy – High Strength, Excellent Machinability & Corrosion Resistance