WL 3.1754 T6 Alloy – Premium Material for Gearboxes & Air Inlet Systems

The high temperature material has good casting capabilities. Due to the hot cracking tendency limited suitability for investment casting. Application: gear boxes, air inlets

Properties

General

PropertyTemperatureValueConditionRelated StandardsShape

Density

2.84 g/cm³

T6

WL 3.1754

Casting

20.0 °C

2.84 g/cm³

T6

WL 3.1854, WL 3.1754

Mechanical

PropertyTemperatureValueConditionRelated StandardsShapeComment

Elastic modulus

70.0 GPa

T6

WL 3.1754

Casting

20.0 °C

70.0 GPa

T6

WL 3.1854, WL 3.1754

Elongation

1.0 %

T6

WL 3.1754

Casting

A50

20.0 °C

1.0 %

T6

WL 3.1854, WL 3.1754

Hardness, Brinell

80.0 [-]

T6

WL 3.1754

Casting

20.0 °C

80.0 [-]

T6

WL 3.1854, WL 3.1754

Poisson's ratio

0.33 [-]

Typical for Cast 2xx.x Series Aluminium

Tensile strength

180.0 MPa

T6

WL 3.1754

Casting

190.0 MPa

T6

WL 3.1754

Casting

20.0 °C

180.0 MPa

T6

WL 3.1854, WL 3.1754

20.0 °C

185.0 MPa

T6

WL 3.1854, WL 3.1754

20.0 °C

190.0 MPa

T6

WL 3.1854, WL 3.1754

20.0 °C

200.0 MPa

T6

WL 3.1854, WL 3.1754

20.0 °C

215.0 MPa

T6

WL 3.1854, WL 3.1754

Thermal

PropertyTemperatureValueConditionRelated StandardsShapeComment

Coefficient of thermal expansion

20 °C

1.9999999999999998e-05 1/K

T6

WL 3.1754

Casting

100 °C

1.9999999999999998e-05 1/K

T6

WL 3.1754

Casting

Melting point

510.0 - 790.0 °C

Typical for Cast 2xx.x Series Aluminium

Specific heat capacity

875.0 - 963.0 J/(kg·K)

Typical for Cast 2xx.x Series Aluminium

Thermal conductivity

155 W/(m·K)

T6

WL 3.1754

Casting

20.0 °C

155.0 W/(m·K)

T6

WL 3.1854, WL 3.1754

Electrical

PropertyTemperatureValueConditionRelated StandardsShape

Electrical conductivity

21000000.0 S/m

T6

WL 3.1754

Casting

20.0 °C

21000000.0 S/m

T6

WL 3.1854, WL 3.1754

Electrical resistivity

4.76e-08 Ω·m

T6

WL 3.1754

Casting

Chemical properties

PropertyValueConditionRelated StandardsShape

Aluminium

93.4 %

T6

WL 3.1854, WL 3.1754

Copper

4.2 - 5.0 %

T6

WL 3.1854, WL 3.1754

4.5 - 5.5 %

T6

WL 3.1754

Casting

Iron

0.35 %

T6

WL 3.1854, WL 3.1754

0.50 %

T6

WL 3.1754

Casting

Magnesium

0.15 - 0.35 %

T6

WL 3.1854, WL 3.1754

Manganese

0.1 %

T6

WL 3.1854, WL 3.1754

0.2 - 0.3 %

T6

WL 3.1754

Casting

Nickel

0.03 %

T6

WL 3.1854, WL 3.1754

1.3 - 1.8 %

T6

WL 3.1754

Casting

Silicon

0.3 %

T6

WL 3.1854, WL 3.1754

Casting

Titanium

0.15 - 0.25 %

T6

WL 3.1854, WL 3.1754

Casting

Zinc

0.1

T6

WL 3.1854, WL 3.1754

Zirconium

0.1 - 0.3 %

T6

WL 3.1754

Casting

Technological properties

Property
Processing methods

investment casting, sample taken from casting


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 1706 AC-44000 F Aluminium Casting Alloy – Key Properties & Standards
    2. EN 1706 Grade AC-44100 F – High-Performance Aluminium Casting Alloy
    3. EN 1706 Grade AC-44200 F Aluminium Casting Alloy – High-Performance, Industrial Grade
    4. EN 1706 AC-44300 F Aluminium Casting Alloy – Key Properties & Standards
    5. EN 1706 AC-44400F Aluminium Casting Alloy – Key Properties & Standards
    6. EN 1706 AC-51200 F Aluminium Casting Alloy – Key Properties & Standards
    7. EN 1706 Grade AC-51300 F – High-Strength Aluminium Casting Alloy
    8. EN 1706 AC-46500 F – Aluminium Die Casting Alloy: Properties & Standards
    9. EN 1706 AC‑46600 F Aluminium Alloy – High‑Strength, Low‑Density Casting Solution
    10. EN 1706 AC-47000 F Aluminium Casting Alloy – Specifications