ASTM B316 Grade 7075 T6 Aluminum Alloy – High Strength & Corrosion Resistance
ASTM 7075 is a high-strength alloy that offers good stress-corrosion cracking resistance. Known as a mainstay in the aerospace industry since it was introduced, Aluminum 7075 brings moderate toughness as well as an excellent strength-to-weight ratio. It is also important to note that at sub-zero temperatures Aluminum 7075 increases in strength.
Additional services: Cuttings, Parts from drawingsSTEEL SCOUT
DISTRIBUTOR
Information and services
Quantity: 1 PCSProperties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.7 - 2.85 g/cm³ | Typical for Wrought 7000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 69.0 - 72.0 GPa | Typical for Wrought 7000 Series Aluminium | |||
Elongation | 6.0 % | T6 | ASTM B316 | Wire, Rod | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 7000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 7000 Series Aluminium | |||
Shear modulus | 26.4 - 27.1 GPa | Typical for Wrought 7000 Series Aluminium | |||
Shear strength | 290.0 MPa | T6 | ASTM B316 | Wire, Rod | |
Tensile strength | 530.0 MPa | T6 | ASTM B316 | Wire, Rod |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.1e-05 - 2.4e-05 1/K | Typical for Wrought 7000 Series Aluminium |
Melting point | 465.0 - 655.0 °C | Typical for Wrought 7000 Series Aluminium |
Specific heat capacity | 795.0 - 1050.0 J/(kg·K) | Typical for Wrought 7000 Series Aluminium |
Thermal conductivity | 121.0 - 170.0 W/(m·K) | Typical for Wrought 7000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 34000000.0 S/m | Typical for Wrought 7000 Series Aluminium |
Electrical resistivity | 2.9e-08 - 5.6e-08 Ω·m | Typical for Wrought 7000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.18 - 0.28 % | T6 | ASTM B316 | Wire, Rod |
Copper | 1.2 - 2.0 % | T6 | ASTM B316 | Wire, Rod |
Iron | 0.5 | T6 | ASTM B316 | Wire, Rod |
Magnesium | 2.1 - 2.9 % | T6 | ASTM B316 | Wire, Rod |
Manganese | 0.3 | T6 | ASTM B316 | Wire, Rod |
Silicon | 0.4 | T6 | ASTM B316 | Wire, Rod |
Titanium | 0.2 | T6 | ASTM B316 | Wire, Rod |
Zinc | 5.1 - 6.1 % | T6 | ASTM B316 | Wire, Rod |
Technological properties
| Property | ||
|---|---|---|
| Brazing | Excellent | |
Metal
- ASTM B316 Grade 7075 – High-Strength Aerospace Aluminum Alloy
- ASTM B316 Grade 7075 Aluminum Alloy – Superior Strength & Corrosion Resistance for Aerospace Applications
- ASTM B316 Grade 3003O Aluminum Alloy: High Corrosion Resistance & Easy Welding
- ASTM B316 Grade 2017 Aluminum Alloy – Strength, Ductility & Machinability
- ASTM B316 Grade 5005 O – High-Performance Aluminum Alloy for Marine and Industrial Use
- ASTM B316 Grade 5052‑O Aluminum Alloy: Superior Corrosion Resistance & Welding Performance
- ASTM B210 Grade 7075O Aluminum – Premium High-Strength Aerospace Alloy
- ASTM B211 Grade 7075-O: Premium Aerospace-Grade Aluminum Alloy
- ASTM B241 Grade 7075 O Aluminum: High-Strength Alloy for Aerospace
- ASTM B316 Grade 7075 T73: Premium Aerospace-Grade Aluminum Alloy