ASTM B316 Grade 2219 T6 – High-Strength Aluminum Alloy for Structural Applications
Aluminum Alloy ASTM 2219, an age-hardenable alloy is produced with a copper additive. It is well-known for its excellent structural strength and it’s used for numerous high temperature applications. It is a suitable alloy for many metalworking processes including machining, forming, heat treatment, cold working, and more.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.75 - 2.84 g/cm³ | Typical for Wrought 2000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 70.0 - 73.0 GPa | Typical for Wrought 2000 Series Aluminium | |||
Elongation | 5.0 % | T6 | ASTM B316 | Wire, Rod | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Shear modulus | 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | |||
Shear strength | 205.0 MPa | T6 | ASTM B316 | Wire, Rod | |
Tensile strength | 380.0 MPa | T6 | ASTM B316 | Wire, Rod |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium |
Melting point | 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium |
Specific heat capacity | 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium |
Thermal conductivity | 112.0 - 251.0 W/(m·K) | Typical for Wrought 2000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Copper | 5.8 - 6.8 % | T6 | ASTM B316 | Wire, Rod |
Iron | 0.3 | T6 | ASTM B316 | Wire, Rod |
Magnesium | 0.02 | T6 | ASTM B316 | Wire, Rod |
Manganese | 0.2 - 0.4 % | T6 | ASTM B316 | Wire, Rod |
Silicon | 0.2 | T6 | ASTM B316 | Wire, Rod |
Titanium | 0.02 - 0.1 % | T6 | ASTM B316 | Wire, Rod |
Zinc | 0.1 | T6 | ASTM B316 | Wire, Rod |
Technological properties
| Property | ||
|---|---|---|
| Workability | Moderate Workability | |
Metal
- ASTM B316 Grade 2117 H15 Aluminum Alloy – Key Properties & Applications
- ASTM B316 Grade 2117 O Aluminium Alloy – Key Properties & Applications
- ASTM B316: Grade 2117 H13 – Key Properties & Standards
- ASTM B316 Grade 5056-O: Premium 5000-Series Aluminum Alloy
- ASTM B316 Grade 2024-O: High‑Strength Aerospace Aluminum Alloy
- ASTM B316 Grade 2219 H13: High-Strength Aluminum Alloy for High-Temperature Applications
- ASTM B316 Grade 1100 O Aluminum Alloy – Superior Corrosion Resistance & Purest 1000 Series
- ASTM B211 Grade 2219 T851 – High-Strength Aluminum Alloy for Advanced Applications
- ASTM B241 Grade 2219O: High-Strength, Age-Hardenable Aluminum Alloy
- AA 2219 Aluminum Alloy – Grade O – High Strength, Heat‑Resistant Structural Grade