ASTM B241 Grade 2219O: High-Strength, Age-Hardenable Aluminum Alloy
Aluminum Alloy ASTM 2219, an age-hardenable alloy is produced with a copper additive. It is well-known for its excellent structural strength and it’s used for numerous high temperature applications. It is a suitable alloy for many metalworking processes including machining, forming, heat treatment, cold working, and more.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.75 - 2.84 g/cm³ | Typical for Wrought 2000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 70.0 - 73.0 GPa | Typical for Wrought 2000 Series Aluminium | |||
Elongation | 10.0 % | O | ASTM B241 | Tube | |
12.0 % | O | ASTM B241 | Tube | A50 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Shear modulus | 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | |||
Tensile strength | 220.0 | O | ASTM B241 | Tube |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium |
Melting point | 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium |
Specific heat capacity | 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium |
Thermal conductivity | 112.0 - 251.0 W/(m·K) | Typical for Wrought 2000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Copper | 5.8 - 6.8 % | O | ASTM B241 | Tube |
Iron | 0.3 | O | ASTM B241 | Tube |
Magnesium | 0.02 | O | ASTM B241 | Tube |
Manganese | 0.2 - 0.4 % | O | ASTM B241 | Tube |
Silicon | 0.2 | O | ASTM B241 | Tube |
Titanium | 0.02 - 0.1 % | O | ASTM B241 | Tube |
Zinc | 0.1 | O | ASTM B241 | Tube |
Technological properties
| Property | ||
|---|---|---|
| Workability | Moderate Workability | |
Metal
- ASTM B241 Grade 5154 O – Premium 5000 Series Aluminum Alloy
- ASTM B316 Grade 2219 H13: High-Strength Aluminum Alloy for High-Temperature Applications
- ASTM B241 Grade 2014 T42 Aluminum Alloy – Superior Strength & Machinability
- ASTM B241 Grade 2219 T62 Aluminum Alloy – High Strength, Temperature‑Resistant Grade for Advanced Applications
- ASTM B241 Grade 6063 O: Premium Corrosion‑Resistant Architectural Aluminum Alloy
- ASTM B211 Grade 2219 T851 – High-Strength Aluminum Alloy for Advanced Applications
- ASTM B241 Grade 2014 Aluminum Alloy (T6, T6510, T6511) – High Strength & Versatility
- ASTM B241 Grade 2014 T62 – Premium 2000 Series Aluminum Alloy
- ASTM B316 Grade 2219 T6 – High-Strength Aluminum Alloy for Structural Applications
- ASTM B241 Grade 2014 O: High-Strength, Machinable Aluminum Alloy