ASTM B241 Grade 2014 Aluminum Alloy (T6, T6510, T6511) – High Strength & Versatility
ASTM 2014 is an alloy with strength, machinability and welding capabilities, Aluminum Alloy ASTM 2014 is an excellent option. It is a precipitation hardening alloy that maintains strength after heat treatment.
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.75 - 2.84 g/cm³ | Typical for Wrought 2000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 70.0 - 73.0 GPa | Typical for Wrought 2000 Series Aluminium | |||
Elongation | 6.0 % | T6, T6510, T6511 | ASTM B241 | Tube | |
7.0 % | T6, T6510, T6511 | ASTM B241 | Tube | A50 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Shear modulus | 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | |||
Tensile strength | 415.0 MPa | T6, T6510, T6511 | ASTM B241 | Tube | |
440.0 MPa | T6, T6510, T6511 | ASTM B241 | Tube |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium |
Melting point | 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium |
Specific heat capacity | 816.0 - 963.0 J/(kg·K) | Typical for Wrought 2000 Series Aluminium |
Thermal conductivity | 112.0 - 251.0 W/(m·K) | Typical for Wrought 2000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 18000000.0 - 30000000.0 S/m | Typical for Wrought 2000 Series Aluminium |
Electrical resistivity | 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.1 | T6, T6510, T6511 | ASTM B241 | Tube |
Copper | 3.9 - 5.0 % | T6, T6510, T6511 | ASTM B241 | Tube |
Iron | 0.7 | T6, T6510, T6511 | ASTM B241 | Tube |
Magnesium | 0.2 - 0.8 % | T6, T6510, T6511 | ASTM B241 | Tube |
Manganese | 0.4 - 1.2 % | T6, T6510, T6511 | ASTM B241 | Tube |
Silicon | 0.5 - 1.2 % | T6, T6510, T6511 | ASTM B241 | Tube |
Titanium | 0.15 | T6, T6510, T6511 | ASTM B241 | Tube |
Zinc | 0.25 | T6, T6510, T6511 | ASTM B241 | Tube |
Technological properties
| Property | ||
|---|---|---|
| Workability | Moderate Workability | |
Metal
- ASTM B241 Grade 6162 T6/T6510/T6511 – High‑Strength 6000 Series Aluminium Tubing
- ASTM B241 Grade 6066 Aluminum Tubes – T6, T6510, T6511 Standards and Properties
- ASTM B210 Grade 2014 O Aluminum Alloy – Superior Strength & Machinability
- ASTM B211 Grade 2014O: High‑Strength, Machinable Aluminum Alloy with Excellent Weldability
- ASTM B241 Grade 2014 T42 Aluminum Alloy – Superior Strength & Machinability
- ASTM B241 Grade 2014 T62 – Premium 2000 Series Aluminum Alloy
- ASTM B241 Grade 7075 Aluminum Alloy (T6, T62, T6510, T6511) – High Strength & Corrosion Resistance
- ASTM B241 Grade 2014 O: High-Strength, Machinable Aluminum Alloy
- ASTM B241 Grade 2014 Aluminum Alloy – T4, T4510, T4511 Designations
- ASTM B241 Grade 2219O: High-Strength, Age-Hardenable Aluminum Alloy